Performance of API 5L X65 in 138 MPa Supercritical CO2

Picture for Performance of API 5L X65 in 138 MPa Supercritical CO2
Available for download

Carbon steels and low alloy steels are the workhorse of several industries where properties such as strength, fracture toughness and weldability play a key role. In addition to these properties, carbon steels are also the most cost effective materials is several applications. Of particular interest is the API 5L X65 which is widely used in oil and gas exploration, production and transportation service.

Product Number: 51323-18863-SG
Author: Shiladitya Paul
Publication Date: 2023
$0.00
$20.00
$20.00

This paper reports the performance of welded API 5L X65 in an aqueous solution pressurized with 138 MPa supercritical CO2. Welded API 5L X65 carbon steel specimen was prepared and exposed to 3.5 wt.% NaCl solution pressurised with 138MPa CO2. The sample was stressed to 100% of 0.2% proof stress using a four-point method. The specimen were extracted transverse to the weld and was tested with the weld root in tension. The test ran at 40°C for 30 days. Post-test visual examination indicated a scale on the surface which was confirmed by microstructural characterization. The SEM micrographs indicated corrosion damage, however, no cracks were seen on the tensile surface of the specimen.

This paper reports the performance of welded API 5L X65 in an aqueous solution pressurized with 138 MPa supercritical CO2. Welded API 5L X65 carbon steel specimen was prepared and exposed to 3.5 wt.% NaCl solution pressurised with 138MPa CO2. The sample was stressed to 100% of 0.2% proof stress using a four-point method. The specimen were extracted transverse to the weld and was tested with the weld root in tension. The test ran at 40°C for 30 days. Post-test visual examination indicated a scale on the surface which was confirmed by microstructural characterization. The SEM micrographs indicated corrosion damage, however, no cracks were seen on the tensile surface of the specimen.

Product tags
Also Purchased
Picture for Material Selection for anthropogenic CO2 injection: mechanical and corrosion performances of steels under dense CO2 with impurities
Available for download

Material Selection for anthropogenic CO2 injection: mechanical and corrosion performances of steels under dense CO2 with impurities

Product Number: 51323-18886-SG
Author: Cécile Millet, Guillaume Néel, Luciana Lima, Diana Rodriguez Barrera
Publication Date: 2023
$20.00

Carbon capture and storage (CCS) are technologies aimed at capturing CO2, followed by transportation to a storage site and injection into one of several types of stable geological formations, to trap and prevent its subsequent emission. Though CO2 transport and injection for Enhanced Oil Recovery (EOR) are known for over 40 years, new challenges arise when the CO2 source is anthropogenic, meaning with a human-cause origin and not natural (as in EOR). EU Directive 2009/31/EC states that CO2 streams from power stations or industrial plants "shall consist overwhelmingly of CO2" but may contain associated incidental substances (e.g., SOx, NOx, O2, H2S).
Picture for Corrosion testing of CRA in simulated CO2 injection well environments
Available for download

Corrosion testing of CRA in simulated CO2 injection well environments

Product Number: 51323-18993-SG
Author: Gaute Svenningsen, Bjørn Helge Morland
Publication Date: 2023
$20.00

The number of CCS projects (planned and in operation) is increasing, and project developers need to provide firm evidence that the proposed material is suitable for these applications.
The petroleum industry has long experience with materials selection for wells, but the conditions for CO2 injection wells are somewhat different from “conventional” oil and gas wells. This is due to the high CO2 content and pressure (up to several hundred bar) which results in low pH condensed water (exact value depends on pressure and temperature, but approximately pH 3.0).
Picture for 09255 Corrosion in Super Critical CO2
Available for download

09255 Corrosion in Super Critical CO2

Product Number: 51300-09255-SG
ISBN: 09255 2009 CP
Author: Feng Gui, Francois Ayello, Narasi Sridhar and Ramgopal Thodla
Publication Date: 2009
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support