This paper describes corrosion rate prediction models for the main corrosion mechanisms of carbon steel in Exploration and Production service. The models succeed earlier work by De Waard, Milliams, and Lotz.
We are unable to complete this action. Please try again at a later time.
If this error continues to occur, please contact AMPP Customer Support for assistance.
Use this error code for reference:
Please login to use Standards Credits*
* AMPP Members receive Standards Credits in order to redeem eligible Standards and Reports in the Store
You are not a Member.
AMPP Members enjoy many benefits, including Standards Credits which can be used to redeem eligible Standards and Reports in the Store.
You can visit the Membership Page to learn about the benefits of membership.
You have previously purchased this item.
Go to Downloadable Products in your AMPP Store profile to find this item.
You do not have sufficient Standards Credits to claim this item.
Click on 'ADD TO CART' to purchase this item.
Your Standards Credit(s)
1
Remaining Credits
0
Please review your transaction.
Click on 'REDEEM' to use your Standards Credits to claim this item.
You have successfully redeemed:
Go to Downloadable Products in your AMPP Store Profile to find and download this item.
A test programme was conducted to study corrosion behaviour of - 1. carbon and low alloy steels, 2. austenitic, martensitic and duplex stainless steels and 3. nickel-based Alloy 718 - in low oxygen content (20 & 200 ppb) seawater.
The NORSOK M-506 is an empirical model based on experiments undertaken in a single phase water flow loop. The data is from experiments with low content of iron ions in the water phase, and the model is thus regarded to give a fair representation of the maximum corrosion rate in a CO2 corrosion controlled system.
Performance of formulations of antifouling coatings to protect carbon steel from effects of microbiologically influenced corrosion (MIC) and marine biofouling in a tropical harbor seawater was assessed by field and laboratory experiments. • Scanning electron microscopy (SEM). • Energy dispersive spectroscopy (EDS). • X-ray diffraction (XRD). • Seawater immersion.
Stress assisted corrosion (SAC) is a major concern for kraft recovery boilers in the pulp and paper industry. A water leak can cause a smelt-water explosion in the boiler. A number of carbon steel tubes showed a deep decarburized layer on the inner surface (water-touched) and also an unusually large grain size at the inner tube surface.
This paper summarizes the Top Ten corrosion issues and examines the controlling factors that affect damage including the effects of operating parameters. Best industry practices used to monitor for problems and to inspect for damage are discussed.
Stress corrosion cracking (SCC) of carbon steel in fuel ethanol service has been observed in an increasing number of failures in the last few years. In the presence of oxygen, all of the samples evaluated in this study produced varying degrees of SCC, except for one of the producer ethanol samples. The reason for the high corrosion potential in this sample is still unknown and more detailed analysis of the sample chemical make-up is needed.
This paper studies the effect of oxygen in methanol on the structures and growth kinetics of iron sulfide scales. Gravimetric weight analysis was used to evaluate the corrosion mechanisms and rates. Scanning Electron Microscope/ Energy Dispersive X-ray Spectrometry (SEM/EDX), Optical Microscope and X-ray Diffraction (XRD) were used to analyze the scale.
Corrosion of carbon steel materials in brine solutions. Model results will be compared with literature data and lab experiments. Conditions will be limited to near neutral pH (5-9), temperature from 22oC to 55oC, and O2 atmospheres up to 101.325 kPa.
A parametric study of sour corrosion was conducted and is presented in this paper to provide a better understanding of corrosion in sour gas environments. Various parameters that are known to affect the corrosion rate were evaluated and their impacts on corrosion rate are discussed.
Evaluation of metal-based structures has relied on atmospheric exposure test sites to determine corrosion resistance in marine environments. This work uses surface chemistry and electrochemical techniques to interpret the chemical changes occurring on low carbon and stainless steel during atmospheric and accelerated corrosion conditions to find a correlation between its accelerated and long-term corrosion performance.
Multiple leaks occurred with a carbon steel pipe carrying hot condensate water (300F and 140 psi). A root cause analysis was performed, including visual and metallographic examination of two failed samples chemical, analysis of weld metal and base metal and chemical analysis of water samples. Results show that flow accelerated corrosion (FAC) was the responsible mechanism leading to the failures.