51318-11199-The Effect of Impurities and Pressure on Oxidation in CO2 at 700°-800°C

Picture for The Effect of Impurities and Pressure on Oxidation in CO2 at 700°-800°C
Available for download

Effects of H2O and SO2 on oxidation in a CO2 environment. Experiments at 1 and 25 bar at 700° to 800°C in CO2, CO2+10%H2O and CO2+10%H2O+0.1%SO2. Alloys S30409, N07230, N07208 and superalloy N07247 exposed. Reaction products were characterized.

Product Number: 51318-11199-SG
Author: B. A. Pint / R. G. Brese / J. R. Keiser
Publication Date: 2018
Industry: Science of Corrosion
$0.00
$20.00
$20.00

Direct-fired or open supercritical CO2 (sCO2) cycles are expected to have impurities that may greatly alter the compatibility of structural alloys in these environments. However, there are no available laboratory facilities to simulate these environments at operating conditions of 750°C and >100 bar. As an initial assessment of the effects of H2O and SO2 on oxidation in a CO2 environment, 500 h experiments were conducted at 1 and 25 bar at 700° and 800°C in CO2, CO2+10%H2O and

CO2+10%H2O+0.1%SO2. Representative structural alloys S30409, N07230, N07208 and superalloy

N07247 were exposed and the reaction products characterized after each exposure. The Ni-based alloys generally formed thin protective oxides at both pressures and only minor changes were observed with the addition of SO2 and/or H2O. As expected, the Fe-based S30409 showed more attack, especially at 800°C. However, at 25 bar the attack was reduced at 800°C compared to the breakaway oxidation at 1 bar. For the addition of SO2 at 800°C, a more protective oxide formed at 1 bar but a thick, duplex Fe-rich oxide formed at 25 bar.

Keywords: carbon dioxide, water vapor, SO2, impurities

Direct-fired or open supercritical CO2 (sCO2) cycles are expected to have impurities that may greatly alter the compatibility of structural alloys in these environments. However, there are no available laboratory facilities to simulate these environments at operating conditions of 750°C and >100 bar. As an initial assessment of the effects of H2O and SO2 on oxidation in a CO2 environment, 500 h experiments were conducted at 1 and 25 bar at 700° and 800°C in CO2, CO2+10%H2O and

CO2+10%H2O+0.1%SO2. Representative structural alloys S30409, N07230, N07208 and superalloy

N07247 were exposed and the reaction products characterized after each exposure. The Ni-based alloys generally formed thin protective oxides at both pressures and only minor changes were observed with the addition of SO2 and/or H2O. As expected, the Fe-based S30409 showed more attack, especially at 800°C. However, at 25 bar the attack was reduced at 800°C compared to the breakaway oxidation at 1 bar. For the addition of SO2 at 800°C, a more protective oxide formed at 1 bar but a thick, duplex Fe-rich oxide formed at 25 bar.

Keywords: carbon dioxide, water vapor, SO2, impurities

Product tags
Also Purchased
Picture for Alloy 699 XA: A new Alloy for Application in Petrochemical Industry under Metal Dusting Condititions
Available for download

51318-11200-Alloy 699 XA: A new Alloy for Application in Petrochemical Industry under Metal Dusting Condititions

Product Number: 51318-11200-SG
Author: Heike Hattendorf / Jutta Kloewer / Alejandra López
Publication Date: 2018
$20.00

Alloy 699 XA is a new alloy, which was developed for application in petrochemical industry under metal dusting conditions at high pressure. It contains 30% chromium and 2% aluminum.
Picture for EFFECT OF ANNEALING TEMPERATURE ON PITTING CORROSION BEHAVIOR OF A LEAN DUPLEX STAINLESS STEEL
Available for download

51318-11201-EFFECT OF ANNEALING TEMPERATURE ON PITTING CORROSION BEHAVIOR OF A LEAN DUPLEX STAINLESS STEEL

Product Number: 51318-11201-SG
Author: P. O. Malta / B. L. Condé / R. F. Assumpção / D. B. Perasoli / D. C. Sicupira / D. B. Santos /
Publication Date: 2018
$20.00

To evaluate the effect of annealing temperature on microstructure, hardness, and pitting corrosion of an UNS S32304 lean duplex stainless steel, using a light optical microscope and cyclic potentiodynamic polarization electrochemical measurements.
Picture for Nondestructive Evaluation for Yield Strength and Toughness of Steel Pipelines
Available for download

51318-11204-Nondestructive Evaluation for Yield Strength and Toughness of Steel Pipelines

Product Number: 51318-11204-SG
Author: S. D. Palkovic / K. Taniguchi / S. C. Bellemare
Publication Date: 2018
$20.00

This paper describes two new and complementary mechanical testing methods recently applied to vintage pipeline steels as input to integrity management.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support