Electrochemical Impedance Spectroscopy (EIS) Analysis of Freshwater Foul-Release Coatings

Electrochemical Impedance Spectroscopy (EIS) Analysis of Freshwater Foul-Release Coatings
Available for download

Foul-release coating systems were examined by electrochemical impedance spectroscopy (EIS) to measure the degradation of coating dielectric properties in immersion. Three-inch by six-inch coated steel coupons were placed in dilute Harrison’s solution (DHS) to simulate constant immersion field conditions. 

Product Number: 41213-789-SG
Author: Bobbi Jo Merten, Allen Skaja, David Tordonato
Publication Date: 2013
Industries: Coatings , Corrosion Monitoring and Control
$0.00
$20.00
$20.00

Foul-release coating systems were examined by electrochemical impedance spectroscopy (EIS) to measure the degradation of coating dielectric properties in immersion. Three-inch by six-inch coated steel coupons were placed in dilute Harrison’s solution (DHS) to simulate constant immersion field conditions. This electrolyte concentration is higher than those observed in the field and serves to accelerate the degradation of the coating system. The experiment duration was two years. EIS is a powerful tool for investigating the evolution of a coating’s dielectric properties. There is some indication that it can be used to predict the estimated service life for a coating system. This has the potential to greatly improve cost efficiency when specifying new systems for use as foul-release industrial maintenance coatings. Reclamation requires fouling mitigation technologies for a variety of uses on their water and power infrastructure. Foul-release coating systems are one solution for this. Of the materials tested thus far, silicones have shown excellent field performance by preventing mussel attachment. The foul-release performance is compared to the results of EIS analysis. The study revealed that a few of the systems also have very high barrier protection—maintaining purely capacitive properties following two years in constant immersion. This is necessary to prevent corrosion of the underlying substrate while in service. The coatings were ranked to estimate their service life in regard to barrier protection and foul-release performance. Traditional two-component epoxy coating systems were utilized as an experimental control.

Foul-release coating systems were examined by electrochemical impedance spectroscopy (EIS) to measure the degradation of coating dielectric properties in immersion. Three-inch by six-inch coated steel coupons were placed in dilute Harrison’s solution (DHS) to simulate constant immersion field conditions. This electrolyte concentration is higher than those observed in the field and serves to accelerate the degradation of the coating system. The experiment duration was two years. EIS is a powerful tool for investigating the evolution of a coating’s dielectric properties. There is some indication that it can be used to predict the estimated service life for a coating system. This has the potential to greatly improve cost efficiency when specifying new systems for use as foul-release industrial maintenance coatings. Reclamation requires fouling mitigation technologies for a variety of uses on their water and power infrastructure. Foul-release coating systems are one solution for this. Of the materials tested thus far, silicones have shown excellent field performance by preventing mussel attachment. The foul-release performance is compared to the results of EIS analysis. The study revealed that a few of the systems also have very high barrier protection—maintaining purely capacitive properties following two years in constant immersion. This is necessary to prevent corrosion of the underlying substrate while in service. The coatings were ranked to estimate their service life in regard to barrier protection and foul-release performance. Traditional two-component epoxy coating systems were utilized as an experimental control.

Product tags
Also Purchased
Evaluation and Prediction of Protective Performance for Epoxy Systems and Epoxy/Polyurethane Systems in Wet and Dry Environments
Available for download

Evaluation and Prediction of Protective Performance for Epoxy Systems and Epoxy/Polyurethane Systems in Wet and Dry Environments

Product Number: 41206-258-SG
Author: Chul-Hwan Lee, Chil-Seok Shin, Kwang-Ki Baek
Publication Date: 2006
$20.00

Current coating practice requires the thickness of anti-corrosion organic coatings to be over 250 for immersion parts of ships and offshore structures and the protective performance of these coatings has been evaluated by destructive and qualitative analysis. Recently, Electrochemical Impedance Spectroscopy (EIS) method has been employed, as an alternative, to evaluate corrosion resistance of organic coatings. This method is characterized as being nondestructive, reproducible, and quantitative in evaluating aging of organic coatings. 
EIS Evaluation of Single Layer Coating Performance in Corrosive Environments
Available for download

EIS Evaluation of Single Layer Coating Performance in Corrosive Environments

Product Number: 51220-257-SG
Author: Donald C. Lawson III
Publication Date: 2020
$20.00

Substrate preparation which includes the removal of contaminates, abrading or etching to create a surface profile via mechanical or chemical methods have a major impact on the adhesion performance of applied coatings. For coatings, a primary performance characteristic is adhesion after exposure to corrosive environments. One of the consequences of corrosion forming under a coating is the loss of adhesion or delamination of the coating. 
Elastrometric Acrylic Coatings for Use on Commercial Structures
Available for download

Elastrometric Acrylic Coatings for Use on Commercial Structures

Product Number: 41213-777-SG
Author: Leo Procopio
Publication Date: 2013
$20.00

The protection of commercial buildings from the elements is a major function of the coatings used in new build and maintenance applications. Waterborne elastomeric acrylic coatings represent an important category of coatings used in both residential and commercial architectural painting. 
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support