51318-11002-Damage Mechanism Study of Severe Corrosion of Carbon Steel Pipe in SAGD Brackish Water Service

Picture for Damage Mechanism Study of Severe Corrosion of Carbon Steel Pipe in SAGD Brackish Water Service
Available for download

The carbon steel lines carrying brackish water associated with a heavy oil SAGD (Steam Assisted Gravity Drainage) operation in Northern Alberta experienced severe localized corrosion. This is a continuation of a previous study of similar failures at a similar facility.

Product Number: 51318-11002-SG
Author: Qiang Liu / Rick Marsden / Gordana Mesar / Brad Small
Publication Date: 2018
Industry: Oil and Gas Production
$0.00
$20.00
$20.00

The carbon steel lines carrying brackish water associated with a heavy oil SAGD (Steam Assisted Gravity Drainage) operation in Northern Alberta experienced severe localized corrosion attack specific to bends, welds, and other locations containing a gas phase. Pinhole leaks occurred after only seven years of service. A comprehensive study was conducted which included consideration of possible damage mechanisms based on flow regime, water chemistry, gas composition, piping elevation changes, and various corrosion product/material analysis.

This paper is a continuation of a previous study3 which was based on similar failures which occurred at similar facility. New findings are discussed regarding how the pipes are damaged. It is concluded that CO2 breakout is the major cause of severe pitting on the bends and preferential weld attack despite a low CO2 concentration of < 30 mg/L in the water. The CO2 breakout under turbulent flow and/or piping elevation changes resulted in corrosion rates up to 1.125 mm/y (45 mpy) at 10°C. In comparison, the De Waard-Milliams model predicted a corrosion rate of only 0.0425 mm/y (1.7 mpy)!

Turbulent flow (Reynolds number is 1.7x105) and depressurization contributed to the CO2 breakout from the water which caused severe corrosion with the protective siderite readily removed. Corrosion occurring at CO2 gas/water/metal boundaries resulted in high pitting rates and corrosion was aggravated with the increase in mass transfer when gas bubbles collapse.

Oxygen corrosion and microbial induced corrosion as secondary damage mechanisms are also discussed in this paper. The corrosion damage mechanism study provides guidance for BW piping/pipeline designs and material selection.

Key words: brackish water (BW), CO2 corrosion, turbulent flow, multiphase flow, bicarbonate, CO2 breakout, De Waard-Milliams

The carbon steel lines carrying brackish water associated with a heavy oil SAGD (Steam Assisted Gravity Drainage) operation in Northern Alberta experienced severe localized corrosion attack specific to bends, welds, and other locations containing a gas phase. Pinhole leaks occurred after only seven years of service. A comprehensive study was conducted which included consideration of possible damage mechanisms based on flow regime, water chemistry, gas composition, piping elevation changes, and various corrosion product/material analysis.

This paper is a continuation of a previous study3 which was based on similar failures which occurred at similar facility. New findings are discussed regarding how the pipes are damaged. It is concluded that CO2 breakout is the major cause of severe pitting on the bends and preferential weld attack despite a low CO2 concentration of < 30 mg/L in the water. The CO2 breakout under turbulent flow and/or piping elevation changes resulted in corrosion rates up to 1.125 mm/y (45 mpy) at 10°C. In comparison, the De Waard-Milliams model predicted a corrosion rate of only 0.0425 mm/y (1.7 mpy)!

Turbulent flow (Reynolds number is 1.7x105) and depressurization contributed to the CO2 breakout from the water which caused severe corrosion with the protective siderite readily removed. Corrosion occurring at CO2 gas/water/metal boundaries resulted in high pitting rates and corrosion was aggravated with the increase in mass transfer when gas bubbles collapse.

Oxygen corrosion and microbial induced corrosion as secondary damage mechanisms are also discussed in this paper. The corrosion damage mechanism study provides guidance for BW piping/pipeline designs and material selection.

Key words: brackish water (BW), CO2 corrosion, turbulent flow, multiphase flow, bicarbonate, CO2 breakout, De Waard-Milliams

Product tags
Also Purchased
Picture for 51318-11003- Nuclear Power Balance of Plant Corrosion Management Strategic Perspectives
Available for download

51318-11003- Nuclear Power Balance of Plant Corrosion Management Strategic Perspectives

Product Number: 51318-11003-SG
Author: Graig Cilluffo / Mehul Gandhi
Publication Date: 2018
$20.00

This paper highlights plant processes and systems where these programs are leveraged, driving corrosion and integrity concerns, inspection and monitoring plans, trending and forecasting tools, and long-term asset integrity investment considerations.

 

 
Picture for Localized Corrosion of Mild Steel under Iron Sulfide Layers in CO2/H2S Environment
Available for download

51318-10990-Localized Corrosion of Mild Steel under Iron Sulfide Layers in CO2/H2S Environment

Product Number: 51318-10990-SG
Author: Saba Navabzadeh Esmaeely / Gheorghe Bota / Bruce Brown / Srdjan Nesic
Publication Date: 2018
$20.00

Mild steel specimens (API 5L X65) were pretreated to form a pyrrhotite layer on the surface using high temperature sulfidation in oil, then exposed to a range of aqueous CO2 and H2S corrosion environments, leading to initiation of localized corrosion.

 
Picture for Corrosion Management and Mechanism Study on SAGD Brackish Water System
Available for download

51314-3809-Corrosion Management and Mechanism Study on SAGD Brackish Water System

Product Number: 51314-3809-SG
ISBN: 3809 2014 CP
Author: Jack Whittaker
Publication Date: 2014
$0.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support