51315-5888-Challenges in Detectability of Amine Stress Cracking of Carbon Steels in Gas Sweetening Plant

Picture for Challenges in Detectability of Amine Stress Cracking of Carbon Steels in Gas Sweetening Plant
Available for download
Product Number: 51315-5888-SG
ISBN: 5888 2015 CP
Author: Saad Al Dhafiri
Publication Date: 2015
$0.00
$0.00
$0.00
Acid gas sweetening plants use various amine solvents (namely primary secondary and tertiary) to selectively remove impurities such as Hydrogen Sulfide (H2S) and or Carbon Dioxide (CO2) from natural gas.The most economical material is carbon steel with the exception of stainless steels and its cladding in areas where high severity of corrosion anticipated in amine treating plants. Change in feed composition operational upsets are not uncommon to amine plants will likely result abnormal corrosion rates in plant equipment and piping.Amine stress cracking in addition to wet H2S damage mechanisms is a known cracking degradation in the amine treaters. Often its detectability is questionable even with advance NDE techniques. The paper describes cracking phenomenon in Lean amine (DEA) exchangers made of carbon steel with post weld heat treatment and challenges to detect mitigate repair of defects and remedial measures.Key words: Gas sweetening amine solvent DEA carbon steel material amine stress corrosion cracking challenges crack detectability.
Acid gas sweetening plants use various amine solvents (namely primary secondary and tertiary) to selectively remove impurities such as Hydrogen Sulfide (H2S) and or Carbon Dioxide (CO2) from natural gas.The most economical material is carbon steel with the exception of stainless steels and its cladding in areas where high severity of corrosion anticipated in amine treating plants. Change in feed composition operational upsets are not uncommon to amine plants will likely result abnormal corrosion rates in plant equipment and piping.Amine stress cracking in addition to wet H2S damage mechanisms is a known cracking degradation in the amine treaters. Often its detectability is questionable even with advance NDE techniques. The paper describes cracking phenomenon in Lean amine (DEA) exchangers made of carbon steel with post weld heat treatment and challenges to detect mitigate repair of defects and remedial measures.Key words: Gas sweetening amine solvent DEA carbon steel material amine stress corrosion cracking challenges crack detectability.
Product tags
Also Purchased
Picture for 98405 STRESS CORROSION CRACKING OF CARBON
Available for download

98405 STRESS CORROSION CRACKING OF CARBON STEELS IN AMINE UNITS

Product Number: 51300-98405-SG
ISBN: 98405 1998 CP
Author: J.J. Gonzalez, S. Hernandez, A Viloria
$20.00
Picture for Amine Corrosion in Gas Sweetening Plant: Causes and Minimization on Real Case Study
Available for download

51316-7187-Amine Corrosion in Gas Sweetening Plant: Causes and Minimization on Real Case Study

Product Number: 51316-7187-SG
ISBN: 7187 2016 CP
Author: hajatolah almasi
Publication Date: 2016
$20.00

This paper is presented as a practical guide to identifying the causes of corrosion in different sections of gas sweetening trains and ways to control and minimize corrosion in amine plants.
Picture for 96394 CORROSIVE AMINE CHARACTERIZATION
Available for download

96394 CORROSIVE AMINE CHARACTERIZATION

Product Number: 51300-96394-SG
ISBN: 96394 1996 CP
Author: H. Lee Craig Jr., B. D. McLaughlin
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support