51314-4271-Underfilm Corrosion Creep and Cathodic Delamination: Under the Microscope

Product Number: 51314-4271-SG
ISBN: 4271 2014 CP
Author: Carl Reed
Publication Date: 2014
$0.00
$0.00
$0.00
A common test for the evaluation of corrosion resistance of coatings over steel substrates is underfilm corrosion creep typically measured by determining how far corrosion emanates on a substrate from a holiday under a coating film when subjected to corrosion conditions. This is a very commonly specified property in coatings specifications.Another test which is somewhat related to underfilm corrosion creep is cathodic delamination. In this instance the distance from a holiday is measured from which the coating can be easily removed from the substrate hence the term “delamination”. The cause of this delamination has been associated with the generation of an alkaline substance produced at the cathodic half cell reaction of the corrosion process. This property however is rarely if ever specified in coatings specifications. This fact is puzzling and somewhat troubling because cathodic delamination has the potential to becoming a serious corrosion issue more so than underfilm corrosion creep.This paper looks at the possible mechanisms of underfilm corrosion creep and cathodic delamination over steel surfaces. Also examined is the relationship between these two properties. The paper further looks into how both of these properties are affected by coatings that are designed to protect steel from corrosion and possible mechanisms of that protection. And finally the key question is asked why is cathodic delamination not specified in coatings specifications? 
A common test for the evaluation of corrosion resistance of coatings over steel substrates is underfilm corrosion creep typically measured by determining how far corrosion emanates on a substrate from a holiday under a coating film when subjected to corrosion conditions. This is a very commonly specified property in coatings specifications.Another test which is somewhat related to underfilm corrosion creep is cathodic delamination. In this instance the distance from a holiday is measured from which the coating can be easily removed from the substrate hence the term “delamination”. The cause of this delamination has been associated with the generation of an alkaline substance produced at the cathodic half cell reaction of the corrosion process. This property however is rarely if ever specified in coatings specifications. This fact is puzzling and somewhat troubling because cathodic delamination has the potential to becoming a serious corrosion issue more so than underfilm corrosion creep.This paper looks at the possible mechanisms of underfilm corrosion creep and cathodic delamination over steel surfaces. Also examined is the relationship between these two properties. The paper further looks into how both of these properties are affected by coatings that are designed to protect steel from corrosion and possible mechanisms of that protection. And finally the key question is asked why is cathodic delamination not specified in coatings specifications? 
Product tags
Also Purchased
Picture for Application of ECDA for Integrity Management of KOC Crude Oil Pipelines
Available for download

51314-4227-Application of ECDA for Integrity Management of KOC Crude Oil Pipelines

Product Number: 51314-4227-SG
ISBN: 4227 2014 CP
Author: Sean Brossia
Publication Date: 2014
$0.00
Picture for Effect of Monoethanolamine (MEA) on the Corrosion Rates of Carbon steels and Stainless Steels in CO2
Available for download

51314-4241-Effect of Monoethanolamine (MEA) on the Corrosion Rates of Carbon steels and Stainless Steels in CO2 Saturated NaCl Solutions

Product Number: 51314-4241-SG
ISBN: 4241 2014 CP
Author: Shyamala R
Publication Date: 2014
$20.00
Picture for Effect of Yield Strength on Stress Corrosion Cracking Growth in Neutron-Irradiated Stainless Steels
Available for download

51314-4231-Effect of Yield Strength on Stress Corrosion Cracking Growth in Neutron-Irradiated Stainless Steels

Product Number: 51314-4231-SG
ISBN: 4231 2014 CP
Author: Yugo Ashida
Publication Date: 2014
$0.00