Pitting failure boundary of duplex stainless steel under sour condition was investigated by electrochemical and immersion tests. Polarization measurements investigate the effect of temperature and H2S on the corrosion behavior.
In this paper, the pitting failure boundary of duplex stainless steel under sour condition was investigated by electrochemical and immersion tests. Polarization measurements are employed to investigate the effect of temperature and H2Son the corrosion behavior of Duplex Stainless Steel. And the pitting susceptibility is estimated by the further analysis of polarization curves and surface characterization. The results show that the pitting resistance of S31803 duplex stainless steel decreases with the increase of temperature and the H2S partial pressure. S31803 duplex stainless steel is pitting sensitive at around 85oC in 50kPa H2S, 130,000ppm Cl- condition.
Key words: Stainless steel, Pitting, Polarization curve, H2S, Immersion test
Lean duplex stainless steel (LDSS) can provide mechanical properties similar to that of duplex stainless steel (DSS) and is less expensive. The focus of this work was to assess the stress corrosion cracking (SCC) and SCC susceptibility of DSS and LDSS in chloride-containing sour water conditions.
We are unable to complete this action. Please try again at a later time.
If this error continues to occur, please contact AMPP Customer Support for assistance.
Use this error code for reference:
Please login to use Standards Credits*
* AMPP Members receive Standards Credits in order to redeem eligible Standards and Reports in the Store
You are not a Member.
AMPP Members enjoy many benefits, including Standards Credits which can be used to redeem eligible Standards and Reports in the Store.
You can visit the Membership Page to learn about the benefits of membership.
You have previously purchased this item.
Go to Downloadable Products in your AMPP Store profile to find this item.
You do not have sufficient Standards Credits to claim this item.
Click on 'ADD TO CART' to purchase this item.
Your Standards Credit(s)
1
Remaining Credits
0
Please review your transaction.
Click on 'REDEEM' to use your Standards Credits to claim this item.
You have successfully redeemed:
Go to Downloadable Products in your AMPP Store Profile to find and download this item.
This paper discusses the detailed inspection, testing, metallurgical analysis and supporting factors from which the most likely cause of pitting corrosion was revealed in the DSS flowline welds.
Two super duplex stainless steels were investigated: a W-free (UNS S32750) and a 2.1 wt% W-containing (UNS S39274) grade. Goals: To study localized corrosion resistance of super duplex stainless steels and how W affects the same.