51318-10634-Study on Ferrite Measurement Methods for Duplex Stainless Steel Welds

Picture for Study on Ferrite Measurement Methods for Duplex Stainless Steel Welds
Available for download

Ferrite measurements are used during welding procedures on duplex stainless steel. We studied the effects on the measured ferrite contents of (1) grid size, (2) number of fields and (3) measurement locations.

 

Product Number: 51318-10634-SG
Author: Nozomi Satake / Mikihiro Sakata / Tomoaki Kiso / Toshiaki Okabe /
Publication Date: 2018
Industry: Materials Selection and Design
$0.00
$20.00
$20.00

When duplex stainless steel (DSS) is applied to welded components, ferrite measurement with manual point count according to ASTM(1) E562 is often used during welding procedure qualification as heat affected zone (HAZ) of the weld tends to have high ferrite content. For this measurement method, there are several testing variables and it seems that standard testing variables are not used for ferrite measurements performed by various fabricators. In this paper, the effects of three major variables described in ASTM E562, which were the grid size i.e. number of testing points in a grid, number of fields and measurement locations, on the measured ferrite contents were studied. Also, ferrite measurement with automatic image analysis according to ASTM E1245 was performed across the fusion line of the weld to compare the ferrite content measured by manual point count according to ASTM E562. In addition to the ferrite measurement, pitting corrosion test according to ASTM G48, Method A was performed on the same sample as the one used for ferrite measurement in order to see where in the weld pitting corrosion occurs. The results have suggested a necessity of establishment of standardized testing variables to be used for ferrite measurement with manual point count according to ASTM E562.

Key words: Duplex Stainless Steel, Welding, Ferrite Content, Point Count, ASTM E562, Image Analysis

When duplex stainless steel (DSS) is applied to welded components, ferrite measurement with manual point count according to ASTM(1) E562 is often used during welding procedure qualification as heat affected zone (HAZ) of the weld tends to have high ferrite content. For this measurement method, there are several testing variables and it seems that standard testing variables are not used for ferrite measurements performed by various fabricators. In this paper, the effects of three major variables described in ASTM E562, which were the grid size i.e. number of testing points in a grid, number of fields and measurement locations, on the measured ferrite contents were studied. Also, ferrite measurement with automatic image analysis according to ASTM E1245 was performed across the fusion line of the weld to compare the ferrite content measured by manual point count according to ASTM E562. In addition to the ferrite measurement, pitting corrosion test according to ASTM G48, Method A was performed on the same sample as the one used for ferrite measurement in order to see where in the weld pitting corrosion occurs. The results have suggested a necessity of establishment of standardized testing variables to be used for ferrite measurement with manual point count according to ASTM E562.

Key words: Duplex Stainless Steel, Welding, Ferrite Content, Point Count, ASTM E562, Image Analysis

Product tags
Also Purchased
Picture for In-service Embrittlement of 25%Cr Super Duplex Stainless Steel
Available for download

51318-10612-In-service Embrittlement of 25%Cr Super Duplex Stainless Steel

Product Number: 51318-10612-SG
Author: Mikihiro Sakata / Ichiro Seshimo / Tomoaki Kiso / Toshiaki Okabe
Publication Date: 2018
$20.00

Metallurgical investigations on a welded sample of 25% Cr super duplex stainless steel (UNS S32750) from a vessel that had operated above 300-350°C (570-660°F) for six months, resulting in brittle fracture.
Picture for 51317--9230- Study on Ferrite Content and Hardness of Thick-Wall 22% Cr Duplex Stainless Steel Welded Joints
Available for download

51317-9230- Study on Ferrite Content and Hardness of Thick-Wall 22% Cr Duplex Stainless Steel Welded Joints

Product Number: 51317-9230-SG
Author: Mikihiro Sakata / Nozomi Satake / Tomoaki Kiso / Usani Ofem
Publication Date: 2017
$20.00

In this study, welding trials were performed on 22% Cr duplex stainless steel UNS S32205 corner joints with different wall thickness similar to the top plate and tubesheet plate joint configuration used in a fin fan cooler header box.
Picture for Effects of nitride precipitation in duplex stainless steel
Available for download

51318-10512-Effects of nitride precipitation in duplex stainless steel

Product Number: 51318-10512-SG
Author: Marco De Marco / Marco Palombo / Anthony Pianezze / Abderrahmane Taiche / Valentina Spinelli / Marina Delucchi
Publication Date: 2018
$20.00

The aim of this paper is to find a correlation between nitride content/distribution and properties of two of the largely adopted Duplex Stainless Steel (DSS), UNS* S32205 and UNS S32750. *Unified Numbering System
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support