51317-9230- Study on Ferrite Content and Hardness of Thick-Wall 22% Cr Duplex Stainless Steel Welded Joints

Picture for 51317--9230- Study on Ferrite Content and Hardness of Thick-Wall 22% Cr Duplex Stainless Steel Welded Joints
Available for download

In this study, welding trials were performed on 22% Cr duplex stainless steel UNS S32205 corner joints with different wall thickness similar to the top plate and tubesheet plate joint configuration used in a fin fan cooler header box.

Product Number: 51317-9230-SG
Author: Mikihiro Sakata / Nozomi Satake / Tomoaki Kiso / Usani Ofem
Publication Date: 2017
Industry: Materials Selection and Design
$0.00
$20.00
$20.00

In refineries and oil and gas plants, air-cooled heat exchangers, so-called fin fan coolers, are fabricated from 22% Cr duplex stainless steels where type 300 series stainless steels would have problems with chloride pitting and chloride stress corrosion cracking (CSCC). Depending on application, limits are often specified for ferrite content and hardness (typically 35-65% for ferrite content and 320 HV maximum) during welding procedure qualification. Recent several cases of failures in hydroprocessing reactor effluent air cooler (REAC) system in refineries are now attracting worldwide attention to ferrite content and hardness in 22% Cr duplex stainless steel welds. In this study, welding trials were performed on 22% Cr duplex stainless steel UNS S32205 corner joints with different wall thickness similar to the top plate and tubesheet plate joint configuration used in a fin fan cooler header box. The effects of material thickness (15 mm, 25 mm, and 35 mm), weld heat input, and joint restraint during welding fabrication on ferrite content and hardness of the welds were evaluated. The results seem to suggest a need for careful re-evaluation of the upper limits of ferrite content and hardness for thick-wall 22% duplex stainless steel joint which are currently used.

 

Key words: Conference papers, 2017 conference papers, 22% Cr duplex stainless steel, welding, ferrite content, hardness, thick-wall

 

In refineries and oil and gas plants, air-cooled heat exchangers, so-called fin fan coolers, are fabricated from 22% Cr duplex stainless steels where type 300 series stainless steels would have problems with chloride pitting and chloride stress corrosion cracking (CSCC). Depending on application, limits are often specified for ferrite content and hardness (typically 35-65% for ferrite content and 320 HV maximum) during welding procedure qualification. Recent several cases of failures in hydroprocessing reactor effluent air cooler (REAC) system in refineries are now attracting worldwide attention to ferrite content and hardness in 22% Cr duplex stainless steel welds. In this study, welding trials were performed on 22% Cr duplex stainless steel UNS S32205 corner joints with different wall thickness similar to the top plate and tubesheet plate joint configuration used in a fin fan cooler header box. The effects of material thickness (15 mm, 25 mm, and 35 mm), weld heat input, and joint restraint during welding fabrication on ferrite content and hardness of the welds were evaluated. The results seem to suggest a need for careful re-evaluation of the upper limits of ferrite content and hardness for thick-wall 22% duplex stainless steel joint which are currently used.

 

Key words: Conference papers, 2017 conference papers, 22% Cr duplex stainless steel, welding, ferrite content, hardness, thick-wall

 

Product tags
Also Purchased
Picture for Study on Ferrite Measurement Methods for Duplex Stainless Steel Welds
Available for download

51318-10634-Study on Ferrite Measurement Methods for Duplex Stainless Steel Welds

Product Number: 51318-10634-SG
Author: Nozomi Satake / Mikihiro Sakata / Tomoaki Kiso / Toshiaki Okabe /
Publication Date: 2018
$20.00

Ferrite measurements are used during welding procedures on duplex stainless steel. We studied the effects on the measured ferrite contents of (1) grid size, (2) number of fields and (3) measurement locations.

 
Picture for Case Study: Solving the Puzzle of 10inch Duplex Stainless Steel Flowline Weld Failure
Available for download

51318-11022-Case Study: Solving the Puzzle of 10inch Duplex Stainless Steel Flowline Weld Failure

Product Number: 51318-11022-SG
Author: Mushaid Nauman, Mohammed Rashid
Publication Date: 2018
$20.00

This paper discusses the detailed inspection, testing, metallurgical analysis and supporting factors from which the most likely cause of pitting corrosion was revealed in the DSS flowline welds.

 
Picture for Effects of nitride precipitation in duplex stainless steel
Available for download

51318-10512-Effects of nitride precipitation in duplex stainless steel

Product Number: 51318-10512-SG
Author: Marco De Marco / Marco Palombo / Anthony Pianezze / Abderrahmane Taiche / Valentina Spinelli / Marina Delucchi
Publication Date: 2018
$20.00

The aim of this paper is to find a correlation between nitride content/distribution and properties of two of the largely adopted Duplex Stainless Steel (DSS), UNS* S32205 and UNS S32750. *Unified Numbering System
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support