51318-10836-Stability of buffer solutions for SSC test in stainless steel OCTG material from experimental approach

Picture for Stability of buffer solutions for SSC test in stainless steel OCTG material from experimental approach
Available for download

The stability of buffer solutions for martensitic stainless steel OCTG material was experimentally evaluated by the scratch repassivation technique in electrochemical measurements.

Product Number: 51318-10836-SG
Author: Yasuhide Ishiguro / Takashi Kawano / Kazuki Fujimura
Publication Date: 2018
Industry: Corrosion Monitoring and Control
$0.00
$20.00
$20.00

As an extended report on buffer stability following the previous paper from a theoretical approach in 2016, this paper focuses on the buffering capability of various test buffer solutions from an experimental viewpoint, and presents experimental data supporting the theoretical results, based on the scratch repassivation behavior in electrochemical measurements. In this paper, the stability of buffer solutions for martensitic stainless steel OCTG material, which corresponds to the ability of the solution to maintain the targeted pH throughout the test duration, was experimentally evaluated by the scratch repassivation technique in electrochemical measurements. The measurements were carried out by using a specially designed electrochemical apparatus with a sharp-pointed crooked dental scaler to make scratches on the surface of stainless steel OCTG material samples in 1 bar CO2-saturated buffer solutions. While rest potential is being measured, a short linear scratch corresponding to artificial pitting corrosion is intentionally applied. The potential drops at the moment of scratching, and then returns to the original rest potential. The stability of the buffer solution is evaluated by the time required for the potential to return to the original level, that is, the time required to repassivate the scratched area. A series of scratch-based electrochemical tests were carried out at pH 3.0, pH 3.5 and pH 4.0 to determine the stability of four kinds of NACE-TM0177-based buffer solutions. The experimental results support the phenomena of buffer stability from the theoretical viewpoint. A buffer solution with a shorter time for repassivation is consistent with the one with a more stable buffering effect from the theoretical approach. Precisely, a rich-rich-pair-based buffer solution, which is composed of a highly-concentrated weak acid and highly-concentrated conjugated base, has greater buffering stability than a lean-lean-pair-based one, which is composed of a dilute weak acid and a dilute conjugated base.

Key words: buffer solution stability, buffer capability, buffering effect, scratch repassivation method, electrochemical measurement, NACE TM0177 test solution, pitting corrosion, Solution-C, highly-pressurized CO2 environment, stainless steel.

As an extended report on buffer stability following the previous paper from a theoretical approach in 2016, this paper focuses on the buffering capability of various test buffer solutions from an experimental viewpoint, and presents experimental data supporting the theoretical results, based on the scratch repassivation behavior in electrochemical measurements. In this paper, the stability of buffer solutions for martensitic stainless steel OCTG material, which corresponds to the ability of the solution to maintain the targeted pH throughout the test duration, was experimentally evaluated by the scratch repassivation technique in electrochemical measurements. The measurements were carried out by using a specially designed electrochemical apparatus with a sharp-pointed crooked dental scaler to make scratches on the surface of stainless steel OCTG material samples in 1 bar CO2-saturated buffer solutions. While rest potential is being measured, a short linear scratch corresponding to artificial pitting corrosion is intentionally applied. The potential drops at the moment of scratching, and then returns to the original rest potential. The stability of the buffer solution is evaluated by the time required for the potential to return to the original level, that is, the time required to repassivate the scratched area. A series of scratch-based electrochemical tests were carried out at pH 3.0, pH 3.5 and pH 4.0 to determine the stability of four kinds of NACE-TM0177-based buffer solutions. The experimental results support the phenomena of buffer stability from the theoretical viewpoint. A buffer solution with a shorter time for repassivation is consistent with the one with a more stable buffering effect from the theoretical approach. Precisely, a rich-rich-pair-based buffer solution, which is composed of a highly-concentrated weak acid and highly-concentrated conjugated base, has greater buffering stability than a lean-lean-pair-based one, which is composed of a dilute weak acid and a dilute conjugated base.

Key words: buffer solution stability, buffer capability, buffering effect, scratch repassivation method, electrochemical measurement, NACE TM0177 test solution, pitting corrosion, Solution-C, highly-pressurized CO2 environment, stainless steel.

Product tags
Also Purchased
Picture for Choice of Buffer Solution for Stainless Steel OCTG at Laboratory Corrosion Test to Carry Out SSC and
Available for download

Choice of Buffer Solution for Stainless Steel OCTG at Laboratory Corrosion Test to Carry Out SSC and SCC Resistance

Product Number: 51317--9288-SG
ISBN: 9288 2017 CP
Author: Yasuhide Ishiguro
Publication Date: 2017
$20.00

This paper reviews a theoretical background of buffer solutions for stainless steel oil country tubular goods materials at laboratory corrosion test, and then the concept is applied to NACE-TM0177-based solution and modified solutions.

 
Picture for Evaluation of MIC research in UST under the influence of biodiesel
Available for download

51318-10838-Evaluation of MIC research in UST under the influence of biodiesel

Product Number: 51318-10838-SG
Author: Elsemiek Croese / Walter de Koning / Leon Overduin / Sabine Doddema / Leo van Kuijl / Van der Heide /
Publication Date: 2018
$20.00

Some 1,401 underground diesel storage tanks were analyzed for average maximum pit depths over the years 2003 till 2016. The results showed that since the addition of biodiesel the average pit depth increased due to Microbiologically Influenced Corrosion (MIC).
Picture for BARE FIELD JOINT FOR SUSBEA PIPELINES A POSSIBLE ALTERNATIVE ?
Available for download

51318-10841-BARE FIELD JOINT FOR SUSBEA PIPELINES A POSSIBLE ALTERNATIVE ?

Product Number: 51318-10841-SG
Author: Gwenaëlle Benoit / Morgan Gouriou / Denis Melot / Jean Vittonato / Nicolas Larché
Publication Date: 2018
$20.00

An experiment to simulate bare field joint configuration under cathodic protection over a long term exposure in seawater on a 3LPE coated pipe section in renewed seawater and half-buried in mud. Results conclude that the bare field joint concept is feasible.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support