The principal objective of this work is to investigate and understand the TLC inhibition mechanism in the presence of diethylamine (DEA) and morpholine. In order to determine possible interactions between the tested amines and the steel surface, the surface charge was investigated by determining the potential of zero charge (PZC).

Product Number: 51316-7274-SG
ISBN: 7274 2016 CP
Author: Zineb Belarbi
Publication Date: 2016
Industry: Corrosion Monitoring and Control
$0.00
$20.00
$20.00

Top-of-the-line corrosion (TLC) has the potential to lead to rapid loss of pipeline integrity. TLC also presents unique challenges in relation to its mitigation. Amine compounds are traditionally used as corrosion inhibitors in packages for mitigating CO2 corrosion of carbon steel. They are also claimed to be effective volatile corrosion inhibitors also the mechanism involved in less clear. The principal objective of this work is to investigate and understand the TLC inhibition mechanism in the presence of diethylamine (DEA) and morpholine. In order to determine possible interactions between the tested amines and the steel surface, the surface charge was investigated by determining the potential of zero charge (PZC). The PZC was measured by means of electrochemical impedance spectroscopy (EIS) in a 1 wt.% NaCl solution at different pH values. The possible inhibitive properties of DEA and morpholine were first tested at the bottom of the line conditions by linear polarization resistance (LPR) and EIS, followed by TLC tests. The weight loss method was used to measure the corrosion rate at the top-of-the-line. After the experiments, the steel surface was characterized by scanning electronic microscopy (SEM). The results were interpreted based on the surface charge and provided key information about the possible mechanisms of adsorption amines (DEA and morpholine) on the steel surface. Results showed that the effect of the selected amines on the corrosion rate could be directly linked to the change in solution pH, both at the top and bottom of the line. Considering that the amines were almost fully protonated in the range of pH tested, their vapor pressures and consequently their concentrations in the condensed water were also very low, limiting further their effect on the corrosion at the top of the line. In addition, DEA and morpholine did not seem to have significant filming properties.

Keywords: downloadable, CO2 corrosion, morpholine, PZC, volatile amine, inhibition

Top-of-the-line corrosion (TLC) has the potential to lead to rapid loss of pipeline integrity. TLC also presents unique challenges in relation to its mitigation. Amine compounds are traditionally used as corrosion inhibitors in packages for mitigating CO2 corrosion of carbon steel. They are also claimed to be effective volatile corrosion inhibitors also the mechanism involved in less clear. The principal objective of this work is to investigate and understand the TLC inhibition mechanism in the presence of diethylamine (DEA) and morpholine. In order to determine possible interactions between the tested amines and the steel surface, the surface charge was investigated by determining the potential of zero charge (PZC). The PZC was measured by means of electrochemical impedance spectroscopy (EIS) in a 1 wt.% NaCl solution at different pH values. The possible inhibitive properties of DEA and morpholine were first tested at the bottom of the line conditions by linear polarization resistance (LPR) and EIS, followed by TLC tests. The weight loss method was used to measure the corrosion rate at the top-of-the-line. After the experiments, the steel surface was characterized by scanning electronic microscopy (SEM). The results were interpreted based on the surface charge and provided key information about the possible mechanisms of adsorption amines (DEA and morpholine) on the steel surface. Results showed that the effect of the selected amines on the corrosion rate could be directly linked to the change in solution pH, both at the top and bottom of the line. Considering that the amines were almost fully protonated in the range of pH tested, their vapor pressures and consequently their concentrations in the condensed water were also very low, limiting further their effect on the corrosion at the top of the line. In addition, DEA and morpholine did not seem to have significant filming properties.

Keywords: downloadable, CO2 corrosion, morpholine, PZC, volatile amine, inhibition

Product tags
Also Purchased
Picture for Top of Line Corrosion Testing for a Gas Field with Acetic Acid and Low CO2
Available for download

51316-7275-Top of Line Corrosion Testing for a Gas Field with Acetic Acid and Low CO2

Product Number: 51316-7275-SG
ISBN: 7275 2016 CP
Author: Gaute Svenningsen
Publication Date: 2016
$20.00

The principal objective of this work is to investigate and understand the TLC inhibition mechanism in the presence of diethylamine (DEA) and morpholine. In order to determine possible interactions between the tested amines and the steel surface, the surface charge was investigated by determining the potential of zero charge (PZC).
Picture for Development of Corrosion Inhibitors for Prevention of Top of the Line Corrosion (TLC)
Available for download

51313-02509-Development of Corrosion Inhibitors for Prevention of Top of the Line Corrosion (TLC)

Product Number: 51313-02509-SG
ISBN: 02509 2013 CP
Author: Ming Shen
Publication Date: 2013
$20.00
Picture for Thiols as Volatile Corrosion Inhibitors for Top of the Line Corrosion
Available for download

Thiols as Volatile Corrosion Inhibitors for Top of the Line Corrosion

Product Number: 51317--9096-SG
ISBN: 9096 2017 CP
Author: Zineb Belarbi
Publication Date: 2017
$20.00

The effectiveness of hexanethiol, decanethiol and 11-mercaptoundecanoic acid for CO2 corrosion inhibition of carbon steel exposed to top of the line conditions has been investigated. Weight loss measurements were used to measure the corrosion rate.

 
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support