51318-10863-Behavior of Titanium Exposed to Fresh and Spent Dilute HF Acid Well Stimulation Fluids

Picture for Behavior of Titanium Exposed to Fresh and Spent Dilute HF Acid Well Stimulation Fluids
Available for download

UNS R56404Titanium exposure to warm, naturally-aerated, dilute, HF-containing, fresh acid mixtures does result in unacceptable, elevated etch rates. Several common inorganic salts such as aluminum, molybdate, and/or borate salts, inhibit this attack.

Product Number: 51318-10863-SG
Author: Ronald W. Schutz / Heath W. Walker
Publication Date: 2018
Industry: Oil and Gas Production
$0.00
$20.00
$20.00

Increasing interest in utilizing hydrofluoric acid (HF) for acid stimulation of offshore wells to improve hydrocarbon productivity has raised acid compatibility concerns with titanium alloy riser system components such as Titanium Stress Joints (TSJs). Recent published lab test findings by the authorsconfirmed that UNS R56404Titanium exposure to warm, naturally-aerated, dilute, HF-containing, fresh acid mixtures does result in unacceptable, elevated etch rates, which dramatically increase with temperature and/or acid concentration. These lab studies, however, also revealed that several common inorganic salts such as aluminum, molybdate, and/or borate salts, can effectively inhibit this attack if added in sufficient molar ratios to free fluoride in these fluids.

Corrosion of titanium in these well stimulation acids may also induce significant absorption and/or penetration of byproduct hydrogen, raising additional concern for hydrogen damage to a stressed component if not properly inhibited. Continued lab acid testing of UNS R56404(1) and UNS R56407 titanium coupons confirms that substantial hydrogen uptake and microstructure-dependent penetration can occur during severe HF-containing acid etching. Primary influencing factors are identified from assessment of the effects of CO2 gas saturation; acid formulation, pH, and temperature; fluid flow; and fresh versus spent acid condition; and are considered with respect to inorganic salt inhibitor effectiveness.

Key words: titanium, well acidizing, acid stimulation, hydrofluoric acid, corrosion inhibitor, hydrogen, corrosion

Increasing interest in utilizing hydrofluoric acid (HF) for acid stimulation of offshore wells to improve hydrocarbon productivity has raised acid compatibility concerns with titanium alloy riser system components such as Titanium Stress Joints (TSJs). Recent published lab test findings by the authorsconfirmed that UNS R56404Titanium exposure to warm, naturally-aerated, dilute, HF-containing, fresh acid mixtures does result in unacceptable, elevated etch rates, which dramatically increase with temperature and/or acid concentration. These lab studies, however, also revealed that several common inorganic salts such as aluminum, molybdate, and/or borate salts, can effectively inhibit this attack if added in sufficient molar ratios to free fluoride in these fluids.

Corrosion of titanium in these well stimulation acids may also induce significant absorption and/or penetration of byproduct hydrogen, raising additional concern for hydrogen damage to a stressed component if not properly inhibited. Continued lab acid testing of UNS R56404(1) and UNS R56407 titanium coupons confirms that substantial hydrogen uptake and microstructure-dependent penetration can occur during severe HF-containing acid etching. Primary influencing factors are identified from assessment of the effects of CO2 gas saturation; acid formulation, pH, and temperature; fluid flow; and fresh versus spent acid condition; and are considered with respect to inorganic salt inhibitor effectiveness.

Key words: titanium, well acidizing, acid stimulation, hydrofluoric acid, corrosion inhibitor, hydrogen, corrosion

Product tags
Also Purchased
Picture for Effective Inorganic Salt Corrosion Inhibitors for Titanium Components Exposed to Dilute Hydrofluoric
Available for download

Effective Inorganic Salt Corrosion Inhibitors for Titanium Components Exposed to Dilute Hydrofluoric Acid Well Stimulation Fluids

Product Number: 51317--8978-SG
ISBN: 8978 2017 CP
Author: Ronald Schutz
Publication Date: 2017
$20.00

This laboratory corrosion test screening program is specifically aimed at identifying practical, common inorganic salts which, when added to warm dilute HF solutions, provides effective corrosion inhibition for UNS R56404(ASTM Grade 29 Titanium).
Picture for Titanium Alloy Stress Corrosion Resistance to Methanol Vapor in Hydrocarbon Gas Export Systems
Available for download

51318-10921-Titanium Alloy Stress Corrosion Resistance to Methanol Vapor in Hydrocarbon Gas Export Systems

Product Number: 51318-10921-SG
Author: Ronald W. Schutz / Birendra Jena / Ramgopal Thodla / Heath W. Walker
Publication Date: 2018
$20.00

Susceptibility of Grades 23 and 29 titanium Tapered Stress Joint (TSJ) forgings to gas phase methanolic Stress Corrosion Cracking (SCC) was measured in deaerated, dry 0-0.5 wt.% and saturated methanol-containing methane gas environments at 25C in a two phase laboratory program.
Picture for ASSESSING THE IMPACT OF INSULATION CHOICE ON CORROSION IN A HIGH HUMIDITY DUAL TEMPERATURE ENVIRONMENT
Available for download

51318-10862-ASSESSING THE IMPACT OF INSULATION CHOICE ON CORROSION IN A HIGH HUMIDITY DUAL TEMPERATURE ENVIRONMENT

Product Number: 51318-10862-SG
Author: Dr. Mark Swift
Publication Date: 2018
$20.00

Details of a second procedure developed by the testing centre INNCOA to assess the performance of several insulation systems with respect to the ingress of water vapour through a damaged section of the covering layer.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support