96245 CORROSION FATIGUE CRACK GROWTH RATE IN SENSITIZED ALLOY 600 IN THIOSULFATE SOLUTION

Picture for 96245 CORROSION FATIGUE CRACK GROWTH
Available for download
Product Number: 51300-96245-SG
ISBN: 96245 1996 CP
Author: Chau-Ching Kuoh , Wen-Ta Tsai, Ju-Tung Lee
Industry: Energy Generation
$0.00
$20.00
$20.00
The corrosion fatigue crack growth (FCG) behavior of sensitized (1100°C/0.5h+ 700°C/5h) Alloy 600 in 0.1M sodium thiosulfate solution at room temperature under applied anodic potential conditions was investigated by employing fracture mechanics technique. The results show that the FCG rate depends on the testing frequency and the potential applied. At a frequency of 1 Hz, the FCG rates were independent of the potential applied and were almost the same as that tested in N2 atmosphere. However, at a frequency of 0.1 Hz, the FCG rate increased with increasing applied potential. The fracture morphology of the corrosion fatigue of sensitized Alloy 600 was decided by the competition of environment and mechanical effect. Keywords: corrosion fatigue, crack growth rate, sensitized alloy 600, thiosulfate solution
The corrosion fatigue crack growth (FCG) behavior of sensitized (1100°C/0.5h+ 700°C/5h) Alloy 600 in 0.1M sodium thiosulfate solution at room temperature under applied anodic potential conditions was investigated by employing fracture mechanics technique. The results show that the FCG rate depends on the testing frequency and the potential applied. At a frequency of 1 Hz, the FCG rates were independent of the potential applied and were almost the same as that tested in N2 atmosphere. However, at a frequency of 0.1 Hz, the FCG rate increased with increasing applied potential. The fracture morphology of the corrosion fatigue of sensitized Alloy 600 was decided by the competition of environment and mechanical effect. Keywords: corrosion fatigue, crack growth rate, sensitized alloy 600, thiosulfate solution
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 96242 PIPELINE STRESS CORROSION CRACKING:
Available for download

96242 PIPELINE STRESS CORROSION CRACKING: CRACK GROWTH SENSITIVITY STUDIES UNDER SIMULATED FIELD CONDITIONS

Product Number: 51300-96242-SG
ISBN: 96242 1996 CP
Author: R. L. Sutherby, M. J. Wilmott , T. R. Jack, G. Van Boven
$20.00
Picture for 96230 SCALE INHIBITION IN DESALINATION
Available for download

96230 SCALE INHIBITION IN DESALINATION APPLICATIONS: AN OVERVIEW

Product Number: 51300-96230-SG
ISBN: 96230 1996 CP
Author: Zahid Amjad
$20.00
Picture for 96246 CATHODIC HYDROGEN EMBRITTLEMENT
Available for download

96246 CATHODIC HYDROGEN EMBRITTLEMENT OF A 22% CHROMIUM 5% NICKEL DUPLEX STAINLESS STEEL IN SULFIDE CONTAINING 3.5 wt%. NaCl SOLUTION

Product Number: 51300-96246-SG
ISBN: 96246 1996 CP
Author: S. Y. Tsai, H. C. Shih, K. P. Yen
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support