09412 Effect of Derofmation and Orientation on SCC of Alloy 690

Picture for 09412 Effect of Derofmation and Orientation on SCC of Alloy 690
Available for download
Product Number: 51300-09412-SG
ISBN: 09412 2009 CP
Author: Martin Morra, John Wilson, Peter L. Andresen, John Hickling and Kawait Ahluwalia
Publication Date: 2009
$0.00
$20.00
$20.00
Alloy 690, of various microstructures and types of cold work, was tested in representative pressurized water reactor primary water at 340 and 360 °C. Intergranular cracking was observed on Alloy 690 at constant stress intensity factor (no cycling) and with “gentle” cyclic loading. Crack growth rates in some cases were in the range of 1 to 10 x 10–9 mm/s, but growth rates as high as 7 x 10–7 mm/s were observed in Alloy 690 with microstructural banding and 1-dimension cold rolling that was tested in the S-L orientation.

Keywords: Stress corrosion cracking, Alloy 690, cold work, microstructural inhomogeneity, banding, PWR, PWSCC, high temperature water
Alloy 690, of various microstructures and types of cold work, was tested in representative pressurized water reactor primary water at 340 and 360 °C. Intergranular cracking was observed on Alloy 690 at constant stress intensity factor (no cycling) and with “gentle” cyclic loading. Crack growth rates in some cases were in the range of 1 to 10 x 10–9 mm/s, but growth rates as high as 7 x 10–7 mm/s were observed in Alloy 690 with microstructural banding and 1-dimension cold rolling that was tested in the S-L orientation.

Keywords: Stress corrosion cracking, Alloy 690, cold work, microstructural inhomogeneity, banding, PWR, PWSCC, high temperature water
Product tags
Also Purchased
Picture for 09411 Stress Corrosion Cracking of Stainless Steels in High Temperature High Purity Water under Cons
Available for download

09411 Stress Corrosion Cracking of Stainless Steels in High Temperature High Purity Water under Constant Load Conditions

Product Number: 51300-09411-SG
ISBN: 09411 2009 CP
Author: Julie B. Eager and Edward Richey
Publication Date: 2009
$20.00
Picture for 09414 Effect of Dissolved H2 on SCC of Ni Alloys and Weld Metals
Available for download

09414 Effect of Dissolved H2 on SCC of Ni Alloys and Weld Metals

Product Number: 51300-09414-SG
ISBN: 09414 2009 CP
Author: Kawait Ahluwalia, Peter L. Andresen, John Wilson and John Hickling
Publication Date: 2009
$20.00
Picture for 09366 Increasing Zirconium's Resistance to Stress Corrosion Cracking and Intergranular Attack in Hot
Available for download

09366 Increasing Zirconium's Resistance to Stress Corrosion Cracking and Intergranular Attack in Hot Concentrated Hydrochloric Acid

Product Number: 51300-09366-SG
ISBN: 09366 2009 CP
Author: Patrick Snow
Publication Date: 2009
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support