08490 Water Effects on Adhesion and Wear Resistance of Chromium Oxide Coatings

Product Number: 51300-08490-SG
ISBN: 08490 2008 CP
Author: Xiaolu Pang and Alex Volinsky
Publication Date: 2008
$0.00
$20.00
$20.00
Nano-scratch and nano-indentation were used to determine hardness, elastic modulus, adhesion, friction and wear resistance of chromium oxide coatings in air and in water. The friction coefficient is higher in water, compared to air, and it increases with the applied normal load, although there are no obvious differences in hardness and elastic modulus in air vs. water. A higher normal load increases the wear volume; while the wear rate decreases with the number of wear cycles due to machining hardening. A reduction in coating adhesion was observed in water when the normal load exceeded a critical value of 1.8 N.
Nano-scratch and nano-indentation were used to determine hardness, elastic modulus, adhesion, friction and wear resistance of chromium oxide coatings in air and in water. The friction coefficient is higher in water, compared to air, and it increases with the applied normal load, although there are no obvious differences in hardness and elastic modulus in air vs. water. A higher normal load increases the wear volume; while the wear rate decreases with the number of wear cycles due to machining hardening. A reduction in coating adhesion was observed in water when the normal load exceeded a critical value of 1.8 N.
Product tags
Also Purchased
Picture for 08492 Effects of Temperature and Humidity on Atmospheric Stress Corrosion Cracking of 304 Stainless
Available for download

08492 Effects of Temperature and Humidity on Atmospheric Stress Corrosion Cracking of 304 Stainless Steel

Product Number: 51300-08492-SG
ISBN: 08492 2008 CP
Author: Hitoshi Hayashibara, Masami Mayuzumi, Yoshihiro Mizutani, and Jun-ichi Tani
Publication Date: 2008
$20.00
Picture for 08500 The Influence of Weld Heat-Affected Zone on Stress Corrosion Cracking of Pipeline Steel in Nea
Available for download

08500 The Influence of Weld Heat-Affected Zone on Stress Corrosion Cracking of Pipeline Steel in Near-Neutral pH Environment

Product Number: 51300-08500-SG
ISBN: 08500 2008 CP
Author: B. Fang, E. Han, J. Wang, W. Ke, R. Eadie, W. Zheng, M. Elboujdaini, and W. Revie
Publication Date: 2008
$20.00
Picture for 08495 A Multi-Scale Approach to Stress Corrosion Cracking Characterization
Available for download

08495 A Multi-Scale Approach to Stress Corrosion Cracking Characterization

Product Number: 51300-08495-SG
ISBN: 08495 2008 CP
Author: Sergio Lozano-Perez
Publication Date: 2008
$20.00