07486 Intergranular Stress Corrosion Cracking of Pump Wear Rings

Picture for 07486 Intergranular Stress Corrosion Cracking of Pump Wear Rings
Available for download
Product Number: 51300-07486-SG
ISBN: 07486 2007 CP
Author: Larry Wong
Publication Date: 2007
$0.00
$20.00
$20.00
This paper addresses the intergranular stress corrosion cracking (IGSCC) problem in the 400 series stainless steel wear rings installed on the pump impeller. The results from the study indicate that the engineering design, the metallurgical heat treatment and the raw water chemical content all contribute to IGSCC problem. The tight interference fit between the ring and the impeller caused high residual stress. The heat treatment of the material at the specified temperatures provided the desirable hardness but also creating weak corrosion resistance near the grain boundary areas. High chloride content was found in the reservoir water serviced by the pump. Failure analysis and evaluation were performed on the failed parts. Samples from the impeller wearing rings were sent to laboratory for examinations. Alternatives and proposals resolving the intergranular stress corrosion cracking problem are discussed.
This paper addresses the intergranular stress corrosion cracking (IGSCC) problem in the 400 series stainless steel wear rings installed on the pump impeller. The results from the study indicate that the engineering design, the metallurgical heat treatment and the raw water chemical content all contribute to IGSCC problem. The tight interference fit between the ring and the impeller caused high residual stress. The heat treatment of the material at the specified temperatures provided the desirable hardness but also creating weak corrosion resistance near the grain boundary areas. High chloride content was found in the reservoir water serviced by the pump. Failure analysis and evaluation were performed on the failed parts. Samples from the impeller wearing rings were sent to laboratory for examinations. Alternatives and proposals resolving the intergranular stress corrosion cracking problem are discussed.
Product tags
Also Purchased
Picture for 09200 Premature Failure of a Nickel Aluminum Bronze Vacuum Pump
Available for download

09200 Premature Failure of a Nickel Aluminum Bronze Vacuum Pump

Product Number: 51300-09200-SG
ISBN: 09200 2009 CP
Author: S. Al-Sulaiman, M. Islam, A. Al-Shamari, S. Al-Karim, A. Al-Mithin, S. Prakash
Publication Date: 2009
$20.00
Picture for 06105 Corrosion problems in seawater pump
Available for download

06105 Corrosion problems in seawater pump caissons. Practical solutions.

Product Number: 51300-06105-SG
ISBN: 06105 2006 CP
Author: Svenn Magne Wigen, Harald Osvoll
$20.00
Picture for Experience with Standard Duplex Stainless Steel Seawater Pump in Arabian Gulf Seawater Conditions
Available for download

51314-3733-Experience with Standard Duplex Stainless Steel Seawater Pump in Arabian Gulf Seawater Conditions

Product Number: 51314-3733-SG
ISBN: 3733 2014 CP
Author: Sivuyile Funani
Publication Date: 2014
$0.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support