Why Do We Record the Attributes of a Coating Failure as a Result of an Adhesion Test?

Why Do We Record the Attributes of a Coating Failure as a Result of an Adhesion Test?
Available for download

International standards, both ISO and ASTM, require that the attributes exhibited during an adhesion test are recorded as part of the results. What are these attributes, how should they be recorded and what value are they to the inspector and applicator in assessing the reason for failure?  This paper looks at all these questions and asks should we be going further than we do in defining the mode of failure.

Product Number: 51220-229-SG
Author: David J Barnes
Publication Date: 2020
Industry: Coatings
$0.00
$20.00
$20.00

International standards, both ISO and ASTM, require that the attributes exhibited during an adhesion test are recorded as part of the results. What are these attributes, how should they be recorded and what value are they to the inspector and applicator in assessing the reason for failure?  This paper looks at all these questions and asks should we be going further than we do in defining the mode of failure.

International standards, both ISO and ASTM, require that the attributes exhibited during an adhesion test are recorded as part of the results. What are these attributes, how should they be recorded and what value are they to the inspector and applicator in assessing the reason for failure?  This paper looks at all these questions and asks should we be going further than we do in defining the mode of failure.

Product tags
Also Purchased
Surface Roughness Profile and its effect on Coating Adhesion and Corrosion Protection
Available for download

Surface Roughness Profile and its effect on Coating Adhesion and Corrosion Protection

Product Number: 51220-238-SG
Author: S. G. Croll
Publication Date: 2020
$20.00

Modern design, manufacturing and field-testing specifications include surface profile and adhesion testing on the assumption that they are linked to long term corrosion prevention. There are a number of careful studies, dating back decades, that find no link between measurements of adhesion and (undercutting) corrosion performance, but other studies do, and the concept remains intuitively appealing and widely assumed.
ADHESION TESTING How much is sufficient?
Available for download

ADHESION TESTING How much is sufficient?

Product Number: 51218-161-SG
Author: Dr. Daniel Totev
Publication Date: 2018
$20.00

Pull-off adhesion testing of coatings is commonly used for product testing and qualification as well as quality control / quality assurance. However, initial adhesion values do not necessarily correlate with service life of coatings or their corrosion protection performance. Adhesion of several product chemistries to steel is examined in this study before and after immersion exposure. Results are presented within the context of laboratory corrosion testing in an effort to investigate the significance of adhesion testing in modern lining systems.
Adhesion Tests and Failure Modes Study on Structural Steel Coatings
Available for download

Adhesion Tests and Failure Modes Study on Structural Steel Coatings

Product Number: 41213-771-SG
Author: Wei Zheng, John J. Myers
Publication Date: 2013
$20.00

Pull-off adhesion behaviors of 15 coating systems in three groups were studied utilizing test method ASTM D4541. Three groups of coating systems included coating systems with organic or inorganic zinc-rich primers, polymeric polyurea coatings, and overcoating systems applied on an existing coating system. 
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support