SSPC-PA 16-2022, Method for Evaluating Scribe Undercutting on Coated Steel Test Panels Following Corrosion Testing

Picture for SSPC-PA 16-2022, Method for Evaluating Scribe Undercutting on Coated Steel Test Panels Following Corrosion Testing
Available for download

This standard allows the user to determine average and observed maximum undercutting values, as well as the frequency of the maximum undercutting on coated steel test panels scribed in accordance with Section 6 of ASTM D1654 using parallel, 100 mm (~4 in) scribes. The standard includes requirements for data collection, analysis, and reporting.

This standard is applicable for evaluation of most types of protective coatings for use on steel. This standard is not applicable to evaluation of thermal sprayed metals and ceramic coatings, hot-dip and electro-coated metal coatings, and tapes.

Product Number: SSPC-PA 16-2022
Publication Date: 2022
Industries: Coatings and Linings , Coatings
$109.00
$109.00
$109.00

Or

This standard allows the user to determine average and observed maximum undercutting values, as well as the frequency of the maximum undercutting on coated steel test panels scribed in accordance with Section 6 of ASTM D1654 using parallel, 100 mm (~4 in) scribes. The standard includes requirements for data collection, analysis, and reporting.

This standard is applicable for evaluation of most types of protective coatings for use on steel. This standard is not applicable to evaluation of thermal sprayed metals and ceramic coatings, hot-dip and electro-coated metal coatings, and tapes.

Keywords: undercutting, steel test panels, coatings, rust creepage

This standard allows the user to determine average and observed maximum undercutting values, as well as the frequency of the maximum undercutting on coated steel test panels scribed in accordance with Section 6 of ASTM D1654 using parallel, 100 mm (~4 in) scribes. The standard includes requirements for data collection, analysis, and reporting.

This standard is applicable for evaluation of most types of protective coatings for use on steel. This standard is not applicable to evaluation of thermal sprayed metals and ceramic coatings, hot-dip and electro-coated metal coatings, and tapes.

Keywords: undercutting, steel test panels, coatings, rust creepage

Product tags
Also Purchased
Picture for SSPC-PA 15-2022, Material and Preparation Requirements for Steel Test Panels Used to Evaluate the Performance of Industrial Coatings
Available for download

SSPC-PA 15-2022, Material and Preparation Requirements for Steel Test Panels Used to Evaluate the Performance of Industrial Coatings

Product Number: SSPC-PA 15-2022
Publication Date: 2022
$109.00

This standard contains requirements for steel panels used to perform tests for evaluation of various performance characteristics of protective coatings applied to steel substrates. Panels meeting requirements of this standard may be used for tests including, but not limited to, natural and accelerated exposure in or out of the laboratory; tests to determine resistance to various chemicals, impact, and abrasion; and tests to characterize properties such as color, gloss, adhesion, and hardness. Requirements for steel composition, panel dimensions, surface preparation, ambient conditions for application and cure of coatings, and location and dimensions of scribes on coated panels are included.
Picture for SSPC-GUIDE 18-2022, Specifier’s Guide for Determining Containment Class and Environmental Monitoring Strategies for Lead Paint Removal Projects
Available for download

SSPC-Guide 18-2022, Specifier’s Guide for Determining Containment Class and Environmental Monitoring Strategies for Lead Paint Removal Projects

Product Number: SSPC-GUIDE 18-2022
Publication Date: 2022
$109.00

This Guide describes a six-step process to assist in determining the type of containment system and the level of environmental monitoring that should be specified on a project-specific basis when removing coatings that contain lead. The selection of the containment and monitoring strategies is based on an assessment of the type of paint removal method that will be used and the potential impact of the operations on the public, other workers in the area, and the environment. Note that local and state codes and regulations must be reviewed and take precedence to any guidance provided in this document.

The guidance provided in this document also applies to coatings containing other hazardous metals such as cadmium and chromium; however, the recommended analytical monitoring is often based on an analysis for lead. Paint chip sampling and testing for lead and other hazardous metals should be undertaken to properly characterize the paint being removed.

This Guide does not cover the selection of paint removal methods, or design of containment/ventilation systems.
Picture for SSPC-PA 2-2022, Procedure for Determining Conformance to Dry Coating Thickness Requirements
Available for download

SSPC-PA 2-2022, Procedure for Determining Conformance to Dry Coating Thickness Requirements

Product Number: SSPC-PA 2-2022
Publication Date: 2022
$109.00

This standard describes a procedure for determining shop or field conformance to a specified coating dry film thickness (DFT) range on ferrous and non-ferrous metal substrates using two types of nondestructive coating thickness gages (Type 1, magnetic pull-off, and Type 2, electronic) described in ASTM D7091

Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support