Hydrogen Permeation and Binding Energy Study on OCTG High Strength Steel

Oil Country Tubular Goods (OCTG) high strength steels are susceptible to hydrogen assisted cracking (HAC) due to hydrogen ingress as a result of exposure to environmental conditions (cathodic protection (CP) and/or H2S environments) and as such are prone to failure. In order to address the potential cracking susceptibility a study was performed to understand fundamental parameters such as steady state hydrogen permeation flux hydrogen concentrations and hydrogen trap binding energies of the high strength steel under charging conditions. Electrochemical permeation testing was performed on unstressed and 80%AYS stressed C110 pipe steel using an applied charging current density of 0.5 mA/cm2 in a 1M H2SO4 test solution at 75 F. Comparisons between the stressed and unstressed samples showed that there were no significant differences in steady state flux (Jss) and calculated hydrogen concentration for this charging condition. Further testing was performed to measure hydrogen uptake and time to saturation under the same charging conditions using the Si Oil Method. Subsequent laser thermal desorption spectroscopy (LTDS) was performed at the saturation point and at several temperature scan rates in order to calculate the hydrogen trap binding energies (Eb). Similar testing was performed on P110 material to assess the possibility that differences in Eb are detectable and relatable to HAC.Key words: High Strength Steels Electrochemical Permeation Testing Hydrogen Assisted Cracking CP environment.

Product Number: 51319-12908-SG
Author: Elizabeth Trillo
Publication Date: 2019
$0.00
$20.00
$20.00
Also Purchased
Picture for 09120 - Hydrogen Effects on High Strength Pipeline Steels
Available for download

09120 Hydrogen Effects on High Strength Pipeline Steels

Product Number: 51300-09120-SG
ISBN: 09120 2009 CP
Author: Jeffrey Xie, Fraser King, Robert Yang
Publication Date: 2009
$20.00
Picture for 04472 A Laboratory Study of Types of Corrosion
Available for download

04472 A Laboratory Study of Types of Corrosion Inducing Hydrogen Permeation through Steel

Product Number: 51300-04472-SG
ISBN: 04472 2004 CP
Author: Frank Dean and Stephen W. Powell, Ion Science Ltd.
$20.00