Hydrogen Embrittlement of SS316L Instrument Tubing in a Hydroprocessing Unit

An unexpected failure of 316L Stainless Steel instrument tubing occurred in a high pressure Hydroprocessing unit resulting in a shutdown of the unit. The tubing system consisted of a compression type fitting commonly used in instrument systems and had only been in service for 3 years when the failure occurred. The failed tubing samples were removed for metallurgical analysis and determination of damage mechanism.   

Metallurgical analysis and finite element analysis of the tubing identified excessive cold working leading to hydrogen embrittlement as the primary mode of failure. This paper details the investigation into the failure to arrive at the root cause and the preventive measures adopted to assess the installed population of tubing in similar service.  

 

Product Number: 51320-14357-SG
Author: Siew Leong Waia, Rajaram Chidambaramb, John Richertc, Jorge Perdomo
Publication Date: 2020
$0.00
$20.00
$20.00
Also Purchased
Picture for Hydrogen Embrittlement Susceptibility of Precipitation Hardened Ni-Alloys
Available for download

51314-3948-Hydrogen Embrittlement Susceptibility of Precipitation Hardened Ni-Alloys

Product Number: 51314-3948-SG
ISBN: 3948 2014 CP
Author: Carlo Malara
Publication Date: 2014
$0.00
Picture for Hydrogen Embrittlement Resistance of High Strength Nickel Alloys for Oil and Gas Service
Available for download

51315-5911-Hydrogen Embrittlement Resistance of High Strength Nickel Alloys for Oil and Gas Service

Product Number: 51315-5911-SG
ISBN: 5911 2015 CP
Author: Stephen McCoy
Publication Date: 2015
$20.00