51318-11124-Effect of low-cycle fatigue on corrosion of welded joint in simulated environment of low pressure nuclear steam turbine

The effect of microstructure evolution induced by low-cycle fatigue behavior on the corrosion of welded joint in the simulated environment of low pressure nuclear steam turbine was comprehensively investigated.

Product Number: 51318-11124-SG
Author: Shuo Weng / Yuhui Huang / Fuzhen Xuan
Publication Date: 2018
Industry: Energy Generation
$0.00
$20.00
$20.00

The effect of microstructure evolution induced by low-cycle fatigue behavior on the corrosion of welded joint in the simulated environment of low pressure nuclear steam turbine was comprehensively investigated. The microstructure evolution was observed through optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). Corrosion susceptibility of welded joint was examined by traditional electrochemical measurement and scanning vibrating electrode technique (SVET) measurement. The traditional electrochemical results showed that weld metal was the most susceptive zone with the lowest corrosion potential and the highest corrosion current density in the welded joint, which was in consistence with the results of SVET. In addition, the corrosion resistance of each zone in the post-low-cycle fatigue specimens was higher than that of as-received specimens, which was caused by the lower dislocation density due to low-cycle fatigue behavior.

Key words: low-cycle fatigue damage; corrosion; welded joint; scanning vibrating electrode technique

The effect of microstructure evolution induced by low-cycle fatigue behavior on the corrosion of welded joint in the simulated environment of low pressure nuclear steam turbine was comprehensively investigated. The microstructure evolution was observed through optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). Corrosion susceptibility of welded joint was examined by traditional electrochemical measurement and scanning vibrating electrode technique (SVET) measurement. The traditional electrochemical results showed that weld metal was the most susceptive zone with the lowest corrosion potential and the highest corrosion current density in the welded joint, which was in consistence with the results of SVET. In addition, the corrosion resistance of each zone in the post-low-cycle fatigue specimens was higher than that of as-received specimens, which was caused by the lower dislocation density due to low-cycle fatigue behavior.

Key words: low-cycle fatigue damage; corrosion; welded joint; scanning vibrating electrode technique

Also Purchased
Picture for 00375 COMPARISON BETWEEN HYDROGEN-ENHANCED
Available for download

00375 COMPARISON BETWEEN HYDROGEN-ENHANCED CORROSION FATIGUE CRACK GROWTH RATES AND CRITICAL DISTANCES AHEAD OF A GROWING CRACK

Product Number: 51300-00375-SG
ISBN: 00375 2000 CP
Author: Sergei A. Shipilov
$20.00
Picture for 01237 ENVIRONMENT ASSISTED CRACKING OF STEAM
Available for download

01237 ENVIRONMENT ASSISTED CRACKING OF STEAM TURBINE STEELS - MODELLING OF CRACK CHEMISTRY

Product Number: 51300-01237-SG
ISBN: 01237 2001 CP
Author: Alan Turnbull
$20.00
Picture for 07RTS5 Current Understanding of Environment Induced Cracking of Steam Turbine Steels
Available for download

07RTS5 Current Understanding of Environment Induced Cracking of Steam Turbine Steels

Product Number: 51300-07RTS5-SG
ISBN: 07RTS5 2007 CP
Author: Alan Turnbull
Publication Date: 2007
$20.00