51313-02580-Development of Sour Service Offshore High Strength and Heavy Wall Line Pipe DSAW Process

Picture for Development of Sour Service Offshore High Strength and Heavy Wall Line Pipe DSAW Process
Available for download
Product Number: 51313-02580-SG
ISBN: 02580 2013 CP
Author: Tribhuwan Kathayat
Publication Date: 2013
$0.00
$20.00
$20.00

Authors: T S Kathayat R. T. Hill Rajesh K. Goyal & J. Raghu Shant

Abstract: The presence of severe corrosive environment along with higher external pressure in Black Sea has led to develop high strength heavy wall line pipe. The paper will cover the successful development of high strength SAWL485 SFDU (33”ODX39.5 mm WT) line pipe manufactured by the JCOE technology. Step wise preventive measures were taken during pipe manufacturing & submerged arc welding processes to control the weld & HAZ hardness which is essential to improve the HIC & SSCC performance of line pipe in severe sour environment. Circumferential residual stress was controlled in order increase the HIC resistance. The welding parameters were closely monitored to obtain higher impact toughness at low temperature in weld and HAZ. The proper selection of wire & flux has resulted average CVN impact > 100 J at -30 °C in weld centerline. The study of weld microstructure showed the co-relation of weld ductility (measured in all-weld specimens) with grain boundary ferrite. The hardness of weld centerline was < 225 HV 10 kg even with overmatching of weld tensile strength.


Plate selection with respect to alloy design and microstructure was critical in obtaining good HIC & SSCC resistance for heavy wall line pipe. Plates were supplied by VoestAlpine Grobblech GmbH Austria. The levels of S<0.0010% & P<0.008% along with low value of (Nb+V+Ti)<0.055% ) Pcm<0.15% and CE<0.38% were obtained in the plates.


Key words: Sour Service Heavy wall HIC SSCC HAZ DSAW CVN SFDU

Authors: T S Kathayat R. T. Hill Rajesh K. Goyal & J. Raghu Shant

Abstract: The presence of severe corrosive environment along with higher external pressure in Black Sea has led to develop high strength heavy wall line pipe. The paper will cover the successful development of high strength SAWL485 SFDU (33”ODX39.5 mm WT) line pipe manufactured by the JCOE technology. Step wise preventive measures were taken during pipe manufacturing & submerged arc welding processes to control the weld & HAZ hardness which is essential to improve the HIC & SSCC performance of line pipe in severe sour environment. Circumferential residual stress was controlled in order increase the HIC resistance. The welding parameters were closely monitored to obtain higher impact toughness at low temperature in weld and HAZ. The proper selection of wire & flux has resulted average CVN impact > 100 J at -30 °C in weld centerline. The study of weld microstructure showed the co-relation of weld ductility (measured in all-weld specimens) with grain boundary ferrite. The hardness of weld centerline was < 225 HV 10 kg even with overmatching of weld tensile strength.


Plate selection with respect to alloy design and microstructure was critical in obtaining good HIC & SSCC resistance for heavy wall line pipe. Plates were supplied by VoestAlpine Grobblech GmbH Austria. The levels of S<0.0010% & P<0.008% along with low value of (Nb+V+Ti)<0.055% ) Pcm<0.15% and CE<0.38% were obtained in the plates.


Key words: Sour Service Heavy wall HIC SSCC HAZ DSAW CVN SFDU

Product tags
Also Purchased
Picture for Rapid Corrosion Test for Detecting Intermetallic Phases in Duplex Stainless Steels
Available for download

51313-02583-Rapid Corrosion Test for Detecting Intermetallic Phases in Duplex Stainless Steels

Product Number: 51313-02583-SG
ISBN: 02583 2013 CP
Author: Troels Mathiesen
Publication Date: 2013
$20.00
Picture for Environmentally Assisted Cracking Resistant Ferritic Steels for Light Water Reactor Applications
Available for download

51313-02599-Environmentally Assisted Cracking Resistant Ferritic Steels for Light Water Reactor Applications

Product Number: 51313-02599-SG
ISBN: 02599 2013 CP
Author: Raul Rebak
Publication Date: 2013
$20.00
Picture for Evaluation of the Seabed Temperature SSC Resistance of Weldable Martensitic 13% Chromium SS
Available for download

51313-02589-Evaluation of the Seabed Temperature SSC Resistance of Weldable Martensitic 13% Chromium SS

Product Number: 51313-02589-SG
ISBN: 02589 2013 CP
Author: Philip Dent
Publication Date: 2013
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support