Server maintenance is scheduled for Saturday, December 21st between 6am-10am CST.

During that time, parts of our website will be affected until maintenance is completed. Thank you for your patience.

Menu
Search
Filters
Close
Menu

Use GIVING24 at checkout to save 20% on eCourses and books (some exclusions apply)!

Corrosion Performance of TDG Coatings for Marine Bridge Application

Picture for Corrosion Performance of TDG Coatings for Marine Bridge Application
Available for download
Product Number: 51315-5942-SG
ISBN: 5942 2015 CP
Author: Md Ahsan Sabbir
Publication Date: 2015
$0.00
$0.00
$0.00
Coating systems for corrosion mitigation of structural steel and reinforcing steel in marine bridge applications have been widely used. However novel materials continue to become available and interest lies in identifying improved material performance for marine bridge applications. Interest in application of Thermal Diffusion Galvanizing (TDG) steel for marine bridge application has been raised. Research in progress in part considered TDG with various industry-recommended top coats for structural steel application. Test parameters included evaluating local coating defects such as abrasion environmental conditions and chloride contamination. Physical parameters such as coating thickness and adhesion were also assessed to elucidate corrosion deterioration mechanisms. Immersion in neutral pH water provided an aggressive environment analogous to coatings on structural steel exposed to wet environments (e.g. pooled runoff water). Simulated concrete pore solution (SPS) pH 13.3 was used to identify performance of coated steel in reinforced concrete applications. Accelerated corrosion tests including salt-fog exposures and outdoor exposures were made to identify the possibility for localized corrosion particularly at defects. Preliminary results showed coating bond strength to be below 1000 psi. Corrosion potentials and corrosion current densities for TDG samples immersed in alkaline solution indicated active condition of the zinc throughout the time of testing even though there was indication of degradation to the top coat.
Coating systems for corrosion mitigation of structural steel and reinforcing steel in marine bridge applications have been widely used. However novel materials continue to become available and interest lies in identifying improved material performance for marine bridge applications. Interest in application of Thermal Diffusion Galvanizing (TDG) steel for marine bridge application has been raised. Research in progress in part considered TDG with various industry-recommended top coats for structural steel application. Test parameters included evaluating local coating defects such as abrasion environmental conditions and chloride contamination. Physical parameters such as coating thickness and adhesion were also assessed to elucidate corrosion deterioration mechanisms. Immersion in neutral pH water provided an aggressive environment analogous to coatings on structural steel exposed to wet environments (e.g. pooled runoff water). Simulated concrete pore solution (SPS) pH 13.3 was used to identify performance of coated steel in reinforced concrete applications. Accelerated corrosion tests including salt-fog exposures and outdoor exposures were made to identify the possibility for localized corrosion particularly at defects. Preliminary results showed coating bond strength to be below 1000 psi. Corrosion potentials and corrosion current densities for TDG samples immersed in alkaline solution indicated active condition of the zinc throughout the time of testing even though there was indication of degradation to the top coat.
Product tags
Also Purchased
Picture for Application of Non-Intrusive Fixed Wireless Thickness Monitoring for Sulfidation Corrosion to Provi
Available for download

51315-6169-Application of Non-Intrusive Fixed Wireless Thickness Monitoring for Sulfidation Corrosion to Provide Improved Data over Conventional Inspection

Product Number: 51315-6169-SG
ISBN: 6169 2015 CP
Author: Daniel Chapman
Publication Date: 2015
$0.00
Picture for Corrosion Investigations in Biogas Plants
Available for download

Corrosion Investigations in Biogas Plants

Product Number: 51315-5878-SG
ISBN: 5878 2015 CP
Author: Ralf Feser
Publication Date: 2015
$0.00

The corrosion processes in biogas power plants investigated. Influence of feeding materials. Long term exposition tests of two stainless steels and galvanized steel. Scanning electron microscopy and metallographic cross sections. Electrochemical measurements.  Results.  Safety.
Picture for Corrosion of Copper Coils in Computer Air Handlers
Available for download

Corrosion of Copper Coils in Computer Air Handlers

Product Number: 51315-5963-SG
ISBN: 5963 2015 CP
Author: Todd Mintz
Publication Date: 2015
$0.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support