Comparison of stress corrosion cracking behavior of Fe13Cr5Ni- and Fe17Cr5.5Ni- based high chromium stainless steels in HPHT CO2 environments

The stress corrosion cracking (SCC) behavior of Fe13Cr5Ni- and Fe17Cr5.5Ni-based alloys in HTHP CO2 environments was investigated through slow strain rate tests (SSRT) and electrochemical methods. The results show that a remarkable decrease in tensile strength and elongation to failure was observed when testing in CO2 environment as compared with air. Fe17Cr5.5Ni-based alloys possessed better SCC resistance than Fe13Cr5Ni-based alloys. The increase of Cr and Ni content tended to enhance the resistance to SCC and pitting corrosion. The SCC behaviors of Fe13Cr5Ni- and Fe17Cr5.5Ni-based alloys were closely associated with the repassivation capacity and the resistance to pitting corrosion.

Product Number: 51320-14695-SG
Author: Yameng Qi, Chunxia Zhang, Zhonghua Zhang
Publication Date: 2020
$0.00
$20.00
$20.00
Also Purchased
Picture for 97202 ELECTROCHEMICAL AND STRESS
Available for download

97202 ELECTROCHEMICAL AND STRESS CORROSION CRACKING BEHAVIOUR OF MICRO-ALLOYED STEELS IN CO2/HCO3- ENVIRONMENT

Product Number: 51300-97202-SG
ISBN: 97202 1997 CP
Author: Ennio Sinigaglia, Marina Cabrini
$20.00
Picture for 01296 LONG-TERM FIELD TESTS OF REFERENCE
Available for download

01296 LONG-TERM FIELD TESTS OF REFERENCE ELECTRODES FOR CONCRETE - TEN YEAR RESULTS

Product Number: 51300-01296-SG
ISBN: 01296 2001 CP
Author: Frank J. Ansuini, James R. Dimond
$20.00
Picture for 00271 CORROSION DETECTION AND MONITORING
Available for download

00271 CORROSION DETECTION AND MONITORING - A REVIEW

Product Number: 51300-00271-SG
ISBN: 00271 2000 CP
Author: Vinod S. Agarwala, Siraj Ahmad
$20.00