Case Studies of Thermal Fatigue Damage in Duplex and Stabilized Stainless Steel

Thermal fatigue is a specific type of fatigue failure mechanism that is induced by cyclic stresses generated due to repetitive fluctuations in the temperature. These temperature change in the material induces thermal expansion (or contraction) and if surrounding material or external constraints hinder this expansion thermal stresses arise. The degree of damage is affected by the magnitude and frequency of the temperature swings and typically appears in the form of one or more surface cracks on the component.This paper presents two case histories of thermal fatigue failure along with detailed metallurgical analysis of stainless steel pressure components in a downstream Aromatics plant.The first case study is on failure of a UNS31803 duplex stainless steel heat exchanger tubing that occurred after four and half years in service. The damage was in the form of multiple parallel circumferential surface cracks with few cracks propagating through the wall thickness of tube. The equipment was subjected to a temperature differential of about 100 deg C every 4 hours of operation during alternate heating & cooling cycle.The second failure discussed is on 6” diameter UNS32100 process piping after around ten years of service. This is primarily a thermal mix point wherein demineralized water is injected in a hot gas stream resulting in a temperature gradient of more than 100 Deg C. The failure mode was also characterized by many circumferential cracks at location of injection as well as about 2-3 diameters downstream injection point.Keywords: Thermal Fatigue Stainless Steel Cyclic stresses Temperature differential

Product Number: 51319-13271-SG
Author: Naif Alabri
Publication Date: 2019
$0.00
$20.00
$20.00
Also Purchased
Picture for 08458 Thermal Fatigue in a De-Superheater Induced by Thermal Loads
Available for download

08458 Thermal Fatigue in a De-Superheater Induced by Thermal Loads

Product Number: 51300-08458-SG
ISBN: 08458 2008 CP
Author: Bakheet Al-Yami
Publication Date: 2008
$20.00
Picture for Strain Based Modeling of Thermal Fatigue at Mix Points
Available for download

Strain Based Modeling of Thermal Fatigue at Mix Points

Product Number: 51312-01134-SG
ISBN: 01134 2012 CP
Author: Vianett B Munoz
Publication Date: 2012
$20.00
Picture for 01115 MODELING CORROSION FATIGUE CRACK
Available for download

01115 MODELING CORROSION FATIGUE CRACK PROPAGATION

Product Number: 51300-01115-SG
ISBN: 01115 2001 CP
Author: G. R. Engelhardt, D. D. Macdonald
$20.00