Analysis Of The Pitting Factor For Predicting Localized Corrosion Of Liquid Radioactive Waste At Elevated Temperatures

Product Number: 51321-16547-SG
Author: Roderick E. Fuentes/ Bruce J. Wiersma/ Crystal. L. Girardot/ Theodore J. Venetz
Publication Date: 2021
$0.00
$20.00
$20.00

Millions of liters of liquid radioactive waste are stored in double shell tanks (DSTs) at Hanford Site. The DSTs were constructed of carbon steel from 1968 to 1986 and have a comprehensive chemical control program which mostly relies on hydroxide additions, thus preventing localized corrosion specially stress corrosion cracking (SCC). Most of the radioactive waste is now below 50 ºC and the pitting factor was determined to provide limits in the control program using significant chemical species in the waste. However, several tanks have reached temperatures up to 75 ºC, so the pitting factor equation may not be adequate to address localized corrosion conditions at higher temperatures than 50 ºC. Using statistical analysis, a series of electrochemical tests were designed and developed to account for the increase in temperature with different chemistries and at pH lower than 13. Additionally, testing was performed to differentiate between the contribution from the halides (i.e., chloride and fluoride) in the pitting factor (PF) equation since we have only been focusing on chloride. Cyclic potentiodynamic polarization (CPP) was used to identify regions of localized corrosion susceptibility at different concentrations of statistically significant chemicals in the waste up to 75 ºC. Using the results of this study, the pitting factor was analyzed and validated for elevated temperatures.

Key words: electrochemical testing, cyclic potentiodynamic polarization, Hanford Site, liquid radioactive waste

Millions of liters of liquid radioactive waste are stored in double shell tanks (DSTs) at Hanford Site. The DSTs were constructed of carbon steel from 1968 to 1986 and have a comprehensive chemical control program which mostly relies on hydroxide additions, thus preventing localized corrosion specially stress corrosion cracking (SCC). Most of the radioactive waste is now below 50 ºC and the pitting factor was determined to provide limits in the control program using significant chemical species in the waste. However, several tanks have reached temperatures up to 75 ºC, so the pitting factor equation may not be adequate to address localized corrosion conditions at higher temperatures than 50 ºC. Using statistical analysis, a series of electrochemical tests were designed and developed to account for the increase in temperature with different chemistries and at pH lower than 13. Additionally, testing was performed to differentiate between the contribution from the halides (i.e., chloride and fluoride) in the pitting factor (PF) equation since we have only been focusing on chloride. Cyclic potentiodynamic polarization (CPP) was used to identify regions of localized corrosion susceptibility at different concentrations of statistically significant chemicals in the waste up to 75 ºC. Using the results of this study, the pitting factor was analyzed and validated for elevated temperatures.

Key words: electrochemical testing, cyclic potentiodynamic polarization, Hanford Site, liquid radioactive waste

Also Purchased
Picture for The Effects Of Particle Size On Solid Particle Erosion Of Elbows In Low Liquid And Annular Multiphase Flows
Available for download

The Effects Of Particle Size On Solid Particle Erosion Of Elbows In Low Liquid And Annular Multiphase Flows

Product Number: 51321-16631-SG
Author: Ghulam Haider/ Jun Zhang/ Siamack A. Shirazi
Publication Date: 2021
$20.00
Picture for 04031 A New Generation of More Surface
Available for download

04031 A New Generation of More Surface Tolerant FBE Coatings

Product Number: 51300-04031-SG
ISBN: 04031 2004 CP
Author: Stephen Edmondson, DuPont Powder Coatings
$20.00
Picture for 02267 APPLICATIONS OF SACRIFICIAL ANODE...
Available for download

02267 APPLICATIONS OF SACRIFICIAL ANODE CATHODIC PROTECTION SYSTEMS FOR HIGHWAY BRIDGES - ONTARIO EXPERIENCE

Product Number: 51300-02267-SG
ISBN: 02267 2002 CP
Author: Alan K.C. Ip and Frank Pianca
$20.00