An Evaluation Of The Ripple Slow Strain Rate (RSSR) Technique For Environmentally Assisted Cracking (EAC) Qualification Of Modified 13Cr-110 Stainless Steel

Product Number: 51321-16675-SG
Author: Jing Ning; Yuhchae Yoon; Brent Sherar
Publication Date: 2021
$0.00
$20.00
$20.00

The ripple-slow strain rate (R-SSR) technique is an alternative screening test to the conventional-SSR
(C-SSR) method. Both methods assess susceptibility to environmentally assisted cracking (EAC) of
corrosion resistant alloys (CRAs) and involve loading a NACE TM0198-compliant tensile specimen to
100% AYS (0.2% proof stress of actual yield strength) at a slowly applied extension rate. While the CSSR
specimen is monotonically strained to failure, a R-SSR tensile specimen is typically loaded to 100%
AYS and subsequently cycled between 80% and 100% AYS until failure or for up to 250 cycles or 1 week
of exposure.
This paper will provide a comprehensive review of the current understanding of the R-SSR technique.
There are only a limited number of publications discussing the utility of the R-SSR technique, because
running a R-SSR test is more complicated than a C-SSR test, and the added phenomenological/
mechanistic value of performing a R-SSR test is unclear. On the one hand, cycling loading may be more
representative of certain in-field service conditions. On the other hand, there is evidence to suggest that
cyclic loading facilitates film rupture during the tensile loading part of the cycle and repassivation of
passive and/or protective film during load reversal, which may influence crack propagation. R-SSR may
also be a better approach for martensitic stainless steels than C-SSR where cumulative strain in the
conventional test may be detrimental to material performance. Regardless of the motivation, there is not
a clearly defined and universally recognized acceptance criteria for assessing EAC resistance/
susceptibility by R-SSR.
A pilot research program was initiated to better understand the value of results generated by R-SSR in
comparison to C-SSR. For this study, mod13Cr-110 alloy was used to evaluate and benchmark the two
techniques. The overall goal of the project was to provide guidance on when to use R-SSR and how to
interpret the test results.

The ripple-slow strain rate (R-SSR) technique is an alternative screening test to the conventional-SSR
(C-SSR) method. Both methods assess susceptibility to environmentally assisted cracking (EAC) of
corrosion resistant alloys (CRAs) and involve loading a NACE TM0198-compliant tensile specimen to
100% AYS (0.2% proof stress of actual yield strength) at a slowly applied extension rate. While the CSSR
specimen is monotonically strained to failure, a R-SSR tensile specimen is typically loaded to 100%
AYS and subsequently cycled between 80% and 100% AYS until failure or for up to 250 cycles or 1 week
of exposure.
This paper will provide a comprehensive review of the current understanding of the R-SSR technique.
There are only a limited number of publications discussing the utility of the R-SSR technique, because
running a R-SSR test is more complicated than a C-SSR test, and the added phenomenological/
mechanistic value of performing a R-SSR test is unclear. On the one hand, cycling loading may be more
representative of certain in-field service conditions. On the other hand, there is evidence to suggest that
cyclic loading facilitates film rupture during the tensile loading part of the cycle and repassivation of
passive and/or protective film during load reversal, which may influence crack propagation. R-SSR may
also be a better approach for martensitic stainless steels than C-SSR where cumulative strain in the
conventional test may be detrimental to material performance. Regardless of the motivation, there is not
a clearly defined and universally recognized acceptance criteria for assessing EAC resistance/
susceptibility by R-SSR.
A pilot research program was initiated to better understand the value of results generated by R-SSR in
comparison to C-SSR. For this study, mod13Cr-110 alloy was used to evaluate and benchmark the two
techniques. The overall goal of the project was to provide guidance on when to use R-SSR and how to
interpret the test results.

Also Purchased
Picture for 10323 Mechanical and Electrochemical Evaluation of HCRAs for Oil and Gas Applications
Available for download

10323 Mechanical and Electrochemical Evaluation of HCRAs for Oil and Gas Applications in Sour Environments

Product Number: 51300-10323-SG
ISBN: 10323 2010 CP
Author: W. Kovacs III, H. Tsaprailis, J. R. Tuggle, S. A. Waters & L. F. Garfias-Mesias
Publication Date: 2010
$20.00
Picture for 05103 Laboratory Testing of Age-Hardenable Alloys
Available for download

05103 Laboratory Testing of Age-Hardenable Alloys 925 and 718, in Sour Gas Environments

Product Number: 51300-05103-SG
ISBN: 05103 2005 CP
Author: Rainer Behrens, Krupp VDM GmbH; Dinesh C. Agarwal, ThyssenKrupp VDM USA Inc.
$20.00
Picture for 03129 OFFSHORE NICKEL ALLOY TUBING HANGER
Available for download

03129 OFFSHORE NICKEL ALLOY TUBING HANGER AND DUPLEX STAINLESS STEEL PIPING FAILURE INVESTIGATIONS

Product Number: 51300-03129-SG
ISBN: 03129 2003 CP
Author: S. Huizinga, B. McLoughlin, W.E. Liek, J.G. de Jong
$20.00