99592 CORROSION BEHAVIOR OF CRA’S IN HIGH DENSITY PACKER FLUIDS AT HIGH TEMPERATURE

Picture for 99592 CORROSION BEHAVIOR OF CRA’S IN HIGH
Available for download
Product Number: 51300-99592-SG
ISBN: 99592 1999 CP
Author: L. Scoppio, M. Barteri, T. Cheldi, M. Ke, S. Massi
Industry: Chemical Inhibitors
$0.00
$20.00
$20.00
Results from an experimental investigation carried out in high density brine packer fluids are presented. Different variables were examined, namely temperature, time of exposure, chemical inhibition and brine composition and density. Tests to compare the performance of different classes of stainless steels were carried out by autoclave exposure under different deareated brines solutions: NaCl/NaBr, CaCI2/CaBr2 and CaBr2/ZnBr2, CaCl2, CaCI2/CaBr2/ZnBr2. General corrosion, localized corrosion (pitting and crevice), galvanic corrosion and resistance to environmental cracking were evaluated both in absence of corrosion inhibitor and with the addition of two different commercial inhibitors. Duplex steels were very resistant to the localized corrosion, although pitting and crevice were present in some combination of brine and temperature. The martensitic steel was very sensitive to the general and the localized corrosion... Keywords: Martensitic stainless steel, Duplex stainless steel, Packer fluids, Completion fluids, Deep wells, Brines, Localized corrosion, Galvanic corrosion, Stress Corrosion Cracking.
Results from an experimental investigation carried out in high density brine packer fluids are presented. Different variables were examined, namely temperature, time of exposure, chemical inhibition and brine composition and density. Tests to compare the performance of different classes of stainless steels were carried out by autoclave exposure under different deareated brines solutions: NaCl/NaBr, CaCI2/CaBr2 and CaBr2/ZnBr2, CaCl2, CaCI2/CaBr2/ZnBr2. General corrosion, localized corrosion (pitting and crevice), galvanic corrosion and resistance to environmental cracking were evaluated both in absence of corrosion inhibitor and with the addition of two different commercial inhibitors. Duplex steels were very resistant to the localized corrosion, although pitting and crevice were present in some combination of brine and temperature. The martensitic steel was very sensitive to the general and the localized corrosion... Keywords: Martensitic stainless steel, Duplex stainless steel, Packer fluids, Completion fluids, Deep wells, Brines, Localized corrosion, Galvanic corrosion, Stress Corrosion Cracking.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99589 EFFECT OF MATERIAL COMPOSITION, TEMPERATURE
Available for download

99589 EFFECT OF MATERIAL COMPOSITION, TEMPERATURE AND POTENTIALS ON CREVICE CORROSION OF LC MARTENSITIC 13% CR STEELS IN WELD SIMULATED AND COLD DEFORMED CONDITIONS

Product Number: 51300-99589-SG
ISBN: 99589 1999 CP
Author: Hans Hoffmeister
$20.00
Picture for 99612 THE OVER 20 YEAR OPERATING EXPERIENCE
Available for download

99612 THE OVER 20 YEAR OPERATING EXPERIENCE WITH CARBON STEEL TUBINGS AT ABU ATTIFEL FIELD. PROBLEMS AND SOLUTIONS

Product Number: 51300-99612-SG
ISBN: 99612 1999 CP
Author: Tiziana Cheldi, K. Rumash, Bruno Bazzoni
$20.00
Picture for 99620 EFFECT OF SULFITE IONS IN N2 AND CO2
Available for download

99620 EFFECT OF SULFITE IONS IN N2 AND CO2 PURGED 0.5 M NACL SOLUTION ON STAINLESS STEELS EXAMINED BY DIFFERENT ELECTROCHEMICAL TECHNIQUES AND BY REFLECTANCE MEASUREMENTS

Product Number: 51300-99620-SG
ISBN: 99620 1999 CP
Author: T.Hemmingsen, N. O.Aagotnes, T. Kroeger-Silseth, N. Kolak and M. Kaik
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support