99471 ELECTROCHEMICAL STUDIES OF NITRATE-INDUCED PITTING IN CARBON STEEL

Product Number: 51300-99471-SG
ISBN: 99471 1999 CP
Author: Philip E. Zapp, John W. Van Zee
$0.00
$20.00
$20.00
The phenomenon of pitting in carbon steel exposed to alkaline solutions of nitrate and chloride was studied with the cyclic potentiodynamic polarization technique. Open-circuit and pitting potentials were measured on specimens of ASTM A537 carbon steel in pH 9.73 salt solutions at 40°C, with and without the inhibiting nitrite ion present. Nitrate is not so aggressive a pitting agent as is chloride. Both nitrate and chloride did induce passivity breakdown and pitting in nitrite-free solutions, but the carbon steel retained passivity in solutions with 0.11-M nitrite even at a nitrate concentration of 2.2 M. Keywords: Localized corrosion, cyclic potentiodynamic polarization, passivity, chloride
The phenomenon of pitting in carbon steel exposed to alkaline solutions of nitrate and chloride was studied with the cyclic potentiodynamic polarization technique. Open-circuit and pitting potentials were measured on specimens of ASTM A537 carbon steel in pH 9.73 salt solutions at 40°C, with and without the inhibiting nitrite ion present. Nitrate is not so aggressive a pitting agent as is chloride. Both nitrate and chloride did induce passivity breakdown and pitting in nitrite-free solutions, but the carbon steel retained passivity in solutions with 0.11-M nitrite even at a nitrate concentration of 2.2 M. Keywords: Localized corrosion, cyclic potentiodynamic polarization, passivity, chloride
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 00382 IMPROVEMENT ON THE SULFIDE STRESS CORROSION
Available for download

00382 IMPROVEMENT ON THE SULFIDE STRESS CORROSION CRACKING PROPERTIES OF HOT ROLLED LINE-PIPE STEELS

Product Number: 51300-00382-SG
ISBN: 00382 2000 CP
Author: Kwang-Seop Ro
$20.00
Picture for 09327 Corrosion Resistance of Various Glass Fiber Reinforcements
Available for download

09327 Corrosion Resistance of Various Glass Fiber Reinforcements

Product Number: 51300-09327-SG
ISBN: 09327 2009 CP
Author: Kevin Spoo
Publication Date: 2009
$20.00
Picture for 98172 EFFECT OF NITRITE CONCENTRATION ON
Available for download

98172 EFFECT OF NITRITE CONCENTRATION ON PIT DEPTH IN CARBON STEEL EXPOSED TO SIMULATED RADIOACTIVE WASTE

Product Number: 51300-98172-SG
ISBN: 98172 1998 CP
Author: Philip E. Zapp
$20.00