99332 Alloy 825 and 718 Gasket Corrosion in Deep Water (500m) Connections

Picture for 99332 Alloy 825 and 718 Gasket Corrosion in
Available for download
Product Number: 51300-99332-SG
ISBN: 99332 1999 CP
Author: C Amon, R Howl & J W Oldfield
Industry: Chemical Inhibitors
$0.00
$20.00
$20.00
Corrosion has been observed on a number of alloy 718 (UNS N07718) and alloy 825 (UNS N08825) gaskets from subsea connections. The gaskets were in contact with either weld overlaid alloy 625 (UNS N06625) or super duplex stainless steel hubs (UNS S32750). A few hubs also showed some limited corrosion in regions where severe gasket corrosion had occurred. Corrosion was more prevalent on jumpers that had been exposed to sea water for a few months at alloy 718 (UNS N07718) gaskets in contact with alloy 625 (UNS N06625) weld overlay. General observations were that short term exposures of up to 20 days did not result in corrosion but longer exposures of 40-50 days resulted in severe attack. A programme of work was carried out to determine the reason for the observed attack and to suggest ways of avoiding it in the future. This paper describes the findings of the study. Kevwords: crevice corrosion, galvanic corrosion, sea water, gaskets, nickel base alloys, stainless steels
Corrosion has been observed on a number of alloy 718 (UNS N07718) and alloy 825 (UNS N08825) gaskets from subsea connections. The gaskets were in contact with either weld overlaid alloy 625 (UNS N06625) or super duplex stainless steel hubs (UNS S32750). A few hubs also showed some limited corrosion in regions where severe gasket corrosion had occurred. Corrosion was more prevalent on jumpers that had been exposed to sea water for a few months at alloy 718 (UNS N07718) gaskets in contact with alloy 625 (UNS N06625) weld overlay. General observations were that short term exposures of up to 20 days did not result in corrosion but longer exposures of 40-50 days resulted in severe attack. A programme of work was carried out to determine the reason for the observed attack and to suggest ways of avoiding it in the future. This paper describes the findings of the study. Kevwords: crevice corrosion, galvanic corrosion, sea water, gaskets, nickel base alloys, stainless steels
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99343 REVIEW OF FAILURE MODES IN HOT-
Available for download

99343 REVIEW OF FAILURE MODES IN HOT-WATER BOILERS

Product Number: 51300-99343-SG
ISBN: 99343 1999 CP
Author: Harvey M. Herro
$20.00
Picture for 99345 THE BASICS AND NOT SO BASICS OF WATER
Available for download

99345 THE BASICS AND NOT SO BASICS OF WATER CORROSION PROCESSES ALTERED BY FLOW CHANGES

Product Number: 51300-99345-SG
ISBN: 99345 1999 CP
Author: Thomas M. Laronge and M. A. (Andy) Ward
$20.00
Picture for 05103 Laboratory Testing of Age-Hardenable Alloys
Available for download

05103 Laboratory Testing of Age-Hardenable Alloys 925 and 718, in Sour Gas Environments

Product Number: 51300-05103-SG
ISBN: 05103 2005 CP
Author: Rainer Behrens, Krupp VDM GmbH; Dinesh C. Agarwal, ThyssenKrupp VDM USA Inc.
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support