99049 Intermetallic-Ceramic Coatings for Metals Protection Against Erosion-Corrosion at High Temperatures

Picture for 99049 Intermetallic-Ceramic Coatings for Metals
Available for download
Product Number: 51300-99049-SG
ISBN: 99049 1999 CP
Author: A. Beliaev, B. Q. Wang and A. Verstak
$0.00
$20.00
$20.00
A series of erosion-corrosion (E-C) tests was carried out on the NiAl-Al2O3 interrnetallic-ceramic coatings deposited with high-velocity oxygen-fiel method (HVOF). The tests attempted to simulate the erosion conditions at the heat exchanger tubes in coal-fired boilers. The E-C behavior of these coatings was investigated and compared with other thermal sprayed coatings. It was found that comparing to other coatings, eroded by the bed ash at 300°C, the HVOF NiAl-40Al2O3 coating exhibited the lowest thickness loss at a 90° impact angle, and was the second best at a 30° impact angle. Eroded by the fly ash under test temperatures 450-600°C, the HVOF NiAl-40Al2O3 coating demonstrated the highest erosion-corrosion resistance at all impact angles of testing. At temperatures below 200°C, the E-C wastage of the HVOF NiAl-40Al2O3 coating had essentially no dependence on temperature. From 200°C to 600°C the coating thickness loss increased and from 600 to 800°C the thickness loss decreased with temperature. The HVOF NiAl-40Al2O3 coating eroded by cracking and chipping brittle mechanism. Keywords: interrnetallic-ceramic temperature coatings, erosion, corrosion, erodent particle, impact angle
A series of erosion-corrosion (E-C) tests was carried out on the NiAl-Al2O3 interrnetallic-ceramic coatings deposited with high-velocity oxygen-fiel method (HVOF). The tests attempted to simulate the erosion conditions at the heat exchanger tubes in coal-fired boilers. The E-C behavior of these coatings was investigated and compared with other thermal sprayed coatings. It was found that comparing to other coatings, eroded by the bed ash at 300°C, the HVOF NiAl-40Al2O3 coating exhibited the lowest thickness loss at a 90° impact angle, and was the second best at a 30° impact angle. Eroded by the fly ash under test temperatures 450-600°C, the HVOF NiAl-40Al2O3 coating demonstrated the highest erosion-corrosion resistance at all impact angles of testing. At temperatures below 200°C, the E-C wastage of the HVOF NiAl-40Al2O3 coating had essentially no dependence on temperature. From 200°C to 600°C the coating thickness loss increased and from 600 to 800°C the thickness loss decreased with temperature. The HVOF NiAl-40Al2O3 coating eroded by cracking and chipping brittle mechanism. Keywords: interrnetallic-ceramic temperature coatings, erosion, corrosion, erodent particle, impact angle
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99048 Corrosion, Erosion-Corrosion and Wear
Available for download

99048 Corrosion, Erosion-Corrosion and Wear Resistance of HVOF Sprayed WC Type Coatings with a Corrosion Resistant Binder

Product Number: 51300-99048-SG
ISBN: 99048 1999 CP
Author: Tone Solem, Trend Rogne and John Berget
$20.00
Picture for 97071 NEW CERAMIC-EPOXY TECHNOLOGY
Available for download

97071 NEW CERAMIC-EPOXY TECHNOLOGY FOR OIL AND GAS DRILLING AND PRODUCTION

Product Number: 51300-97071-SG
ISBN: 97071 1997 CP
Author: J. L. Boyd, J. E. Freeman
$20.00
Picture for 99047 CORROSION AND WEAR RESISTANCE OF TUNGSTEN
Available for download

99047 CORROSION AND WEAR RESISTANCE OF TUNGSTEN CARBIDE - COBALT AND TUNGSTEN CARBIDE - COBALT - CHROMIUM THERMAL SPRAY COATINGS.

Product Number: 51300-99047-SG
ISBN: 99047 1999 CP
Author: J. Quets and J. R. Alford
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support