Server maintenance is scheduled for Saturday, December 21st between 6am-10am CST.

During that time, parts of our website will be affected until maintenance is completed. Thank you for your patience.

Menu
Search
Filters
Close
Menu

98627 ELECTROLESS NICKEL COATINGS FOR CORROSION PROTECTlON IN CHLORINE SERVlCE

Picture for 98627 ELECTROLESS NICKEL COATINGS FOR CORROSION
Available for download
Product Number: 51300-98627-SG
ISBN: 98627 1998 CP
Author: ROBERT TRACY, GERALD EVARTS, MARY MUKHTARIAN, WILLIAM McNABB
$0.00
$20.00
$20.00
High phosphorus electroless nickel (HPEN) protects cast and fabricated parts from erosion- corrosion in chlorine gas containing moisture. The reduced corrosion rate ofibrs added protection against metal-chlorine tires that can occur with steel above 185°C (365%). When the moisture content of chlorine exceeds the dew point at a specific metal temperature and a separate phase is formed, severe corrosion of steel occurs. HPEN provides complete protection of steel up to 3000 ppm water in chlorine at 20°C and up to 8000 ppm at 100°C that is well above the dew point of the chlorine/water- mixture for each temperature. HPEN is ideal for protecting chlorine compressor parts fabricated from steel and cast iron Keywords: electroless nickel, chlorine, dry chlorine, steel, compressors, surface preparation, specification, process control
High phosphorus electroless nickel (HPEN) protects cast and fabricated parts from erosion- corrosion in chlorine gas containing moisture. The reduced corrosion rate ofibrs added protection against metal-chlorine tires that can occur with steel above 185°C (365%). When the moisture content of chlorine exceeds the dew point at a specific metal temperature and a separate phase is formed, severe corrosion of steel occurs. HPEN provides complete protection of steel up to 3000 ppm water in chlorine at 20°C and up to 8000 ppm at 100°C that is well above the dew point of the chlorine/water- mixture for each temperature. HPEN is ideal for protecting chlorine compressor parts fabricated from steel and cast iron Keywords: electroless nickel, chlorine, dry chlorine, steel, compressors, surface preparation, specification, process control
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 05232 Corrosion Resistance of UNS NO4400 vs.
Available for download

05232 Corrosion Resistance of UNS NO4400 vs. Electroless Nickel in Simulated Marine Service

Product Number: 51300-05232-SG
ISBN: 05232 2005 CP
Author: Robert D. Klassen and Pierre R. Roberge, Royal Military College; Yueping Wang, DRDC Atlantic
Publication Date: 2005
$20.00

UNS N04400 cladding on steel valves can corrode during marine service.  The uniform corrosion rate of an EN coating in artificial seawater was measured by electrochemical impedance spectroscopy and was found to be less than that for N04400. The main conclusion is that an EN coating could be a viable solution to repair N04400-clad valves in-situ.

 
Picture for 05207 Study on Corrosion Resistance of Electroless
Available for download

05207 Study on Corrosion Resistance of Electroless Plating Ni-P Complex Coating

Product Number: 51300-05207-SG
ISBN: 05207 2005 CP
Author: Huang Yan-bin, Wu Chun-sheng, Liu De-gang, Liang Zhi-jie, Shi Xiao-jun, Zhang Qi-Yong, and Lu Ya-hui
$20.00
Picture for 98708 EFFECT OF CHLORINE ON COMMON MATERIALS
Available for download

98708 EFFECT OF CHLORINE ON COMMON MATERIALS IN FRESH WATER

Product Number: 51300-98708-SG
ISBN: 98708 1998 CP
Author: Arthur H. Tuthill, Richard E. Avery, Stephen Lamb, Gregory Kobrin
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support