98372 ELECTROCHEMICAL NOISE MEASUREMENTS ON CARBON AND STAINLESS STEEL REINFORCING STEELS

Picture for 98372 ELECTROCHEMICAL NOISE MEASUREMENTS ON CARBON
Available for download
Product Number: 51300-98372-SG
ISBN: 98372 1998 CP
Author: M. Tullmin, C.M. Hansson
$0.00
$20.00
$20.00
Electrochemical noise measurements were performed on carbon steel and two stainless alloys exposed to a synthetic pore solution at various pH levels. The test results have confirmed the results of other initial research, that stainless steel rebars are significantly more corrosion resistant compared with the carbon steel variety. The performance of the S3 1600 (UNS) alloy was, as expected, the best of the three alloys evaluated and this stainless steel withstood 160/0 Cl at a pH below 10 in these short term tests. Obviously, corrosive attack could be anticipated at longer test duration and these tests are essentially limited to a relative ranking of the alloys. The 12% Cr alloy also performed distinctly better than the carbon steel but was inferior to the more highly alloyed and costly S3 1600 grade. The electrochemical noise measurements appear to hold much promise for providing ‘early warning’ of imminent rebar corrosion damage and are recommended for field use evaluation. A more complete picture of dynamic rebar corrosion processes is obtained from real-time data, compared with isolated “once-off’ measurements.
Electrochemical noise measurements were performed on carbon steel and two stainless alloys exposed to a synthetic pore solution at various pH levels. The test results have confirmed the results of other initial research, that stainless steel rebars are significantly more corrosion resistant compared with the carbon steel variety. The performance of the S3 1600 (UNS) alloy was, as expected, the best of the three alloys evaluated and this stainless steel withstood 160/0 Cl at a pH below 10 in these short term tests. Obviously, corrosive attack could be anticipated at longer test duration and these tests are essentially limited to a relative ranking of the alloys. The 12% Cr alloy also performed distinctly better than the carbon steel but was inferior to the more highly alloyed and costly S3 1600 grade. The electrochemical noise measurements appear to hold much promise for providing ‘early warning’ of imminent rebar corrosion damage and are recommended for field use evaluation. A more complete picture of dynamic rebar corrosion processes is obtained from real-time data, compared with isolated “once-off’ measurements.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 98351 A Fifteen Year Exposure Study of a
Available for download

98351 A Fifteen Year Exposure Study of a Weathering Steel Bridge

Product Number: 51300-98351-SG
ISBN: 98351 1998 CP
Author: Ann Chidester Van Orden, Robert H. Heidersbach
$20.00
Picture for 98370 A NEW ELECTROCHEMICAL NOISE TECHNIQUE
Available for download

98370 A NEW ELECTROCHEMICAL NOISE TECHNIQUE FOR MONITORING THE LOCALIZED CORROSION OF 304 STAINLESS STEEL IN CHLORIDE- CONTAINING SOLUTIONS

Product Number: 51300-98370-SG
ISBN: 98370 1998 CP
Author: Melissa L. Benish, Janusz Sikora, Barbam Shaw, Elzbieta Sikora, Max Yaffe, Abe Krebs, Gregory Martin
$20.00
Picture for 98373 ELECTROCHEMICAL
Available for download

98373 ELECTROCHEMICAL NOISE ANALYSIS OF GALVANIZED STEEL IMMERSED IN SATURATED Ca(OH)2 SOLUTIONS.

Product Number: 51300-98373-SG
ISBN: 98373 1998 CP
Author: L. Diaz-Ballote, L.F. Garfias-Mesias
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support