98185 CORROSION OF IRON ALUMINIZES IN HCI CONTAINING COAL GASIFICATION ENVIRONMENTS

Picture for 98185 CORROSION OF IRON ALUMINIZES IN HCI
Available for download
Product Number: 51300-98185-SG
ISBN: 98185 1998 CP
Author: W.T. Bakker
$0.00
$20.00
$20.00
Iron aluminizes, both in the form of diffusion coatings on low alloy steels, as well as in alloy or weld overlay form have generally shown excellent corrosion resistance in laboratory tests simulating gasifier and other reducing environments in energy conversion systems. However, the performance of aluminized coatings in gasifiers has generally been unacceptable. Coatings, containing up to 30%Al near the surface, were quite often totally destroyed in 2000-5000 hrs exposure. Here we report on laboratory corrosion tests to elucidate this discrepancy. Both high pressure (41 atm) and atmospheric pressure tests were carried out. The test confirmed the excellent corrosion resistance of iron aluminide in reducing gases containing H2S, even when significant quantities of HCl are present. However, iron aluminizes were found to be extremely susceptible to aqueous corrosion during downtime. Moreover once the protective scale was destroyed, it did not reform easily. Concentration of chloride species at the metal surface during downtime is considered the root cause of the scale degradation mechanism. Keywords: Sulfidation, Oxidation,Chlorination, Iron aluminizes, Stainless Steel, Gasifiers
Iron aluminizes, both in the form of diffusion coatings on low alloy steels, as well as in alloy or weld overlay form have generally shown excellent corrosion resistance in laboratory tests simulating gasifier and other reducing environments in energy conversion systems. However, the performance of aluminized coatings in gasifiers has generally been unacceptable. Coatings, containing up to 30%Al near the surface, were quite often totally destroyed in 2000-5000 hrs exposure. Here we report on laboratory corrosion tests to elucidate this discrepancy. Both high pressure (41 atm) and atmospheric pressure tests were carried out. The test confirmed the excellent corrosion resistance of iron aluminide in reducing gases containing H2S, even when significant quantities of HCl are present. However, iron aluminizes were found to be extremely susceptible to aqueous corrosion during downtime. Moreover once the protective scale was destroyed, it did not reform easily. Concentration of chloride species at the metal surface during downtime is considered the root cause of the scale degradation mechanism. Keywords: Sulfidation, Oxidation,Chlorination, Iron aluminizes, Stainless Steel, Gasifiers
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 98192 LABORATORY STUDIES OF THE CORROSION
Available for download

98192 LABORATORY STUDIES OF THE CORROSION OF NICKEL - BASED ALLOYS BY PURE CALCIUM SULPHATE - INFLUENCE OF ENVIRONMENTAL FACTORS

Product Number: 51300-98192-SG
ISBN: 98192 1998 CP
Author: M. J. Pomeroy, A. Farhat, P. McHale
$20.00
Picture for 98187 THE EFFECTS OF RAPID THERMAL CYCLING
Available for download

98187 THE EFFECTS OF RAPID THERMAL CYCLING ON THE CORROSION OF SOME HIGH-TEMPERATURE ALLOYS IN A SIMULATED COAL-GASIFICATION ENVIRONMENT

Product Number: 51300-98187-SG
ISBN: 98187 1998 CP
Author: F.H. Stott, C.R. Williams
$20.00
Picture for 98197 CORROSION ASPECTS IN THE DESIGN AND
Available for download

98197 CORROSION ASPECTS IN THE DESIGN AND OPERATION OF ODS INDIRECT FIRED HEAT EXCHANGERS

Product Number: 51300-98197-SG
ISBN: 98197 1998 CP
Author: F. Starr
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support