97462 COMPARISON AND CONTRAST: HYDROGEN DAMAGE VS. CREEP FAILURE IN WATERWALL TUBES

Picture for 97462 COMPARISON AND CONTRAST: HYDROGEN
Available for download
Product Number: 51300-97462-SG
ISBN: 97462 1997 CP
Author: Andrew G. Howell
$0.00
$20.00
$20.00
A description of the distinctions between hydrogen damage and metal creep failures of waterwall boiler tubes is given. These two failure modes have many similarities in their origin and superficial characteristics, but the failure mechanisms are very different. In some instances, both mechanisms may occur in the same failure, and may each contribute, to some extent, to the failure. The presence of each failure mechanism results from distinctive root causes, and proper recognition of the failure mode(s) will influence the course of action prescribed to minimize future failures. Keywords: boiler tube failure, hydrogen damage, creep, deposits, equilibrium phosphate, intergranular, waterwall tubing, chemical cleaning
A description of the distinctions between hydrogen damage and metal creep failures of waterwall boiler tubes is given. These two failure modes have many similarities in their origin and superficial characteristics, but the failure mechanisms are very different. In some instances, both mechanisms may occur in the same failure, and may each contribute, to some extent, to the failure. The presence of each failure mechanism results from distinctive root causes, and proper recognition of the failure mode(s) will influence the course of action prescribed to minimize future failures. Keywords: boiler tube failure, hydrogen damage, creep, deposits, equilibrium phosphate, intergranular, waterwall tubing, chemical cleaning
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 11394 Damage Mechanisms in Creep Strength Enhanced Ferritic (CSEF) Steels (T91 and T23)
Available for download

11394 Damage Mechanisms in Creep Strength Enhanced Ferritic (CSEF) Steels (T91 and T23)

Product Number: 51300-11394-SG
ISBN: 2011 11394 CP
Author: Catherine A. Noble and Ronald E. Munson
Publication Date: 2011
$20.00
Picture for Creep Rupture of a Hydrogen Production Reformer Outlet Header of Nickel Base Alloy
Available for download

51313-02369-Creep Rupture of a Hydrogen Production Reformer Outlet Header of Nickel Base Alloy

Product Number: 51313-02369-SG
ISBN: 02369 2013 CP
Author: Laxma Reddy Kethi Reddy
Publication Date: 2013
$20.00
Picture for Creep and Hydrogen Resistant Grade 91 (9Cr1MoV) Heavy Plates for High Efficiency Refining Reactors
Available for download

51313-02230-Creep and Hydrogen Resistant Grade 91 (9Cr1MoV) Heavy Plates for High Efficiency Refining Reactors

Product Number: 51313-02230-SG
ISBN: 02230 2013 CP
Author: Pillot Sylvain
Publication Date: 2013
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support