97232 BOND STRENGTH OF THERMAL-SPRAYED ZINC ON CONCRETE DURING EARLY ELECTROCHEMICAL AGING

Picture for 97232 BOND STRENGTH OF THERMAL-SPRAYED
Available for download
Product Number: 51300-97232-SG
ISBN: 97232 1997 CP
Author: Sophie J. Bullard, Bernard S. Covino, Jr.,Gordon R. Holcomb, Stephen D. Cramer, Galen E. McGill
$0.00
$20.00
$20.00
The Albany Research Center, in collaboration with the Oregon Department of Transportation, is studying changes in the bond strength of thermal-sprayed zinc anodes on reinforced concrete during the early stages of electrochemical aging in impressed current cathodic protection (CP) systems where the zinc surface was not wetted. The bond strength of the zinc to the concrete decreased more rapidly with electrochemical aging when the zinc surface was not wetted than when wetted. The zinc-concrete interfacial chemistry for samples not wetted showed a greater buildup of choride and only weak evidence of secondary mineralization. pH at the zinc-concrete interface was around 7, which was similar to that measured for wetted surfaces. pH at the steel-concrete interface dld not change on aging, remained strongly basic, and was similiar to that for wetted samples. Keywords: cathodic protection, thermal spray, zinc, concrete, steel, electrochemical aging, PH, mineralization, bond strength, bridges, sandblasting
The Albany Research Center, in collaboration with the Oregon Department of Transportation, is studying changes in the bond strength of thermal-sprayed zinc anodes on reinforced concrete during the early stages of electrochemical aging in impressed current cathodic protection (CP) systems where the zinc surface was not wetted. The bond strength of the zinc to the concrete decreased more rapidly with electrochemical aging when the zinc surface was not wetted than when wetted. The zinc-concrete interfacial chemistry for samples not wetted showed a greater buildup of choride and only weak evidence of secondary mineralization. pH at the zinc-concrete interface was around 7, which was similar to that measured for wetted surfaces. pH at the steel-concrete interface dld not change on aging, remained strongly basic, and was similiar to that for wetted samples. Keywords: cathodic protection, thermal spray, zinc, concrete, steel, electrochemical aging, PH, mineralization, bond strength, bridges, sandblasting
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 98510 FIELD PERFORMANCE OF SPRAYED ZINC
Available for download

98510 FIELD PERFORMANCE OF SPRAYED ZINC ANODES IN CONTROLLING CORROSION OF STEEL REINFORCED CONCRETE

Product Number: 51300-98510-SG
ISBN: 98510 1998 CP
Author: Jack Tinnea
$20.00
Picture for 00795 ZINC MESH CATHODIC PROTECTION SYSTEMS
Available for download

00795 ZINC MESH CATHODIC PROTECTION SYSTEMS

Product Number: 51300-00795-SG
ISBN: 00795 2000 CP
Author: Douglas L. Leng, Rodney G. Powers and Ivan R. Lasa
$20.00
Picture for 96308 BOND STRENGTH OF ELECTROCHEMICALLY-
Available for download

96308 BOND STRENGTH OF ELECTROCHEMICALLY-AGED ARC-SPRAYED ZINC COATINGS ON CONCRETE

Product Number: 51300-96308-SG
ISBN: 96308 1996 CP
Author: Bernard S. Covino, Jr,, Sophie J. Bullard, Gordon R. Holcomb, Stephen D. Cramer, Galen E. McGill, Cu
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support