97184 EARLY STAGES OF INTERGRANULAR STRESS CORROSION CRACKING

Picture for 97184 EARLY STAGES OF INTERGRANULAR
Available for download
Product Number: 51300-97184-SG
ISBN: 97184 1997 CP
Author: R.H.Jones, E.P.Simonen, R.E.Williford
$0.00
$20.00
$20.00
Environment-induced crack growth generally progresses through several stages prior to component failure. Early stages of localized corrosion (crack initiation), and short crack growth are early stages in crack development that are summarized in this paper. The implications of these stages on component reliability derive from the extended time that the crack exists in the early stages because crack velocity is low. The duration of the early stages provides a greater opportunity for corrective action if short cracks can be detected. Several Important reasons for understanding short crack behavior are: 1) component life prediction requires a knowledge of the total life cycle of the crack includingthe early stages, 2) greater Pellablility is possible if the transition between short and long crack behavior is known since component life after this transition is short and 3) remedial actions are often more effective for short than long cracks. Keywords: Localized corrosion, stress corrosion, early stages, in-situ, Type 304SS.
Environment-induced crack growth generally progresses through several stages prior to component failure. Early stages of localized corrosion (crack initiation), and short crack growth are early stages in crack development that are summarized in this paper. The implications of these stages on component reliability derive from the extended time that the crack exists in the early stages because crack velocity is low. The duration of the early stages provides a greater opportunity for corrective action if short cracks can be detected. Several Important reasons for understanding short crack behavior are: 1) component life prediction requires a knowledge of the total life cycle of the crack includingthe early stages, 2) greater Pellablility is possible if the transition between short and long crack behavior is known since component life after this transition is short and 3) remedial actions are often more effective for short than long cracks. Keywords: Localized corrosion, stress corrosion, early stages, in-situ, Type 304SS.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 98264 OCCURRENCE OF INTERGRANULAR STRESS
Available for download

98264 OCCURRENCE OF INTERGRANULAR STRESS CORROSION CRACKING IN INDUSTRIAL SYSTEMS

Product Number: 51300-98264-SG
ISBN: 98264 1998 CP
Author: R.H. Jones
$20.00
Picture for 97192 MECHANISTIC DIFFERENCES IN TRANSGRANULAR
Available for download

97192 MECHANISTIC DIFFERENCES IN TRANSGRANULAR AND INTERGRANULAR CRACKING OF AUSTENITIC STAINLESS STEELS

Product Number: 51300-97192-SG
ISBN: 97192 1997 CP
Author: Vimal H. Desai
$20.00
Picture for 00370 RESEARCH CHALLENGES REGARDING STRESS
Available for download

00370 RESEARCH CHALLENGES REGARDING STRESS-CORROSION CRACKING OF PIPELINES

Product Number: 51300-00370-SG
ISBN: 00370 2000 CP
Author: R. R. Fessler, K. Krist
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support