97061 SLOW STRAIN RATE TESTING OF CORROSION RESISTANT ALLOYS IN HIGH TEMPERATURE H2S ENVIRONMENTS

Picture for 97061 SLOW STRAIN RATE TESTING OF CORROSION
Available for download
Product Number: 51300-97061-SG
ISBN: 97061 1997 CP
Author: K. Saarinen, E. Hamalainen, H. Hanninen
$0.00
$20.00
$20.00
To evaluate the effects of manufacturing method and contents of afloying elements on sulfide stress cracking (SSC) behavior, powder metallurgically (PM) produced and wrought super austenitic stainless steels (UNS S32654) and nickel-base alloy UNS N06625 (PM) were studied in high temperature H2S solutions by using slow strain rate tests (SSRT). Attention was paid also to the effects of strain rate on SSC susceptibility of the studied stainless steels. The testing environments were selected based on the proposed, but not yet approved NACE standard test method. According to the SSRT results the studied super austenitic stainless steels showed brittle fracture behavior in all of the studied aggressive H2S solutions. The partial pressures of hydrogen sulfide and carbon dioxide used were over 14 bar. The studied nickel-base alloy was not susceptible to SSC even in H2S solution when the partial pressure of H2S was 70 bar and the partial pressure of CO2 was 50 bar. Keywords: Stainless steel, nickel-base alloy, corrosion, stress corrosion, cracking (fracturing), petrochemical environments, oil fields, hydrogen sulfide
To evaluate the effects of manufacturing method and contents of afloying elements on sulfide stress cracking (SSC) behavior, powder metallurgically (PM) produced and wrought super austenitic stainless steels (UNS S32654) and nickel-base alloy UNS N06625 (PM) were studied in high temperature H2S solutions by using slow strain rate tests (SSRT). Attention was paid also to the effects of strain rate on SSC susceptibility of the studied stainless steels. The testing environments were selected based on the proposed, but not yet approved NACE standard test method. According to the SSRT results the studied super austenitic stainless steels showed brittle fracture behavior in all of the studied aggressive H2S solutions. The partial pressures of hydrogen sulfide and carbon dioxide used were over 14 bar. The studied nickel-base alloy was not susceptible to SSC even in H2S solution when the partial pressure of H2S was 70 bar and the partial pressure of CO2 was 50 bar. Keywords: Stainless steel, nickel-base alloy, corrosion, stress corrosion, cracking (fracturing), petrochemical environments, oil fields, hydrogen sulfide
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99588 WET H&3PERFORMANCE OF AS DELIVERED AND
Available for download

99588 WET H2S PERFORMANCE OF AS DELIVERED AND QUENCHED MODIFIED MARTENSITIC STAINLESS STEELS DETERMINED BY SSRT

Product Number: 51300-99588-SG
ISBN: 99588 1999 CP
Author: T. Tanski, Th. Boellinghaus and H. Hoffmeister
$20.00
Picture for 97048 RAPID SCREENING OF STAINLESS STEELS FOR
Available for download

97048 RAPID SCREENING OF STAINLESS STEELS FOR ENVIRONMENTALLY ASSISTED CRACKING IN H2S/CO2/Cl- ENVIRONMENTS USING THE SLOW STRAIN RATE TEST

Product Number: 51300-97048-SG
ISBN: 97048 1997 CP
Author: C.J.B.M. Joia, A.L.L.T. Small, J.A.C. Ponciano, R.D. Kane
$20.00
Picture for 97130 SLOW STRAIN RATE TESTING OF CARBON
Available for download

97130 SLOW STRAIN RATE TESTING OF CARBON STEEL IN SOLUTIONS WITH HIGH NITRATE CONCENTRATIONS

Product Number: 51300-97130-SG
ISBN: 97130 1997 CP
Author: J. I. Mickalonis
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support