96543 MOLTEN SALT ATTACK OF ALLOY 800H AND CAST STAINLESS STEEL SUPERHEATER COMPONENTS RESULTING FROM STEAM-SIDE CARRYOVER DEPOSITION

Picture for 96543 MOLTEN SALT ATTACK OF ALLOY 800H AND
Available for download
Product Number: 51300-96543-SG
ISBN: 96543 1996 CP
Author: Joseph P. Ribble, Mel J. Esmacher
$0.00
$20.00
$20.00
Three failure analyses involving iron-nickel-chromium alloys (Alloy 800H and niobium modified HP-40) in high temperature steam service 1300°F to 1450°F (704°C to 788°C) arc presented. Boiler water carryover conditions led to steam-side salt deposits containing sodium, chlorine, and sulfur species. The unique conditions of extremely high temperatures and localized accumulation of aggressive salt species resulted in component failures that involved a molten salt attack mechanism not typically observed in steam-side environments. Keywords: Alloy 800H, UNS No. NO8810, UNS No. N08811, Incoloy 800H, HP-40, HP-40Nb, niobium modified HP-40, molten salt attack, mixed molten salt attack, steam-side failures, iron-nickel-chromium alloys.
Three failure analyses involving iron-nickel-chromium alloys (Alloy 800H and niobium modified HP-40) in high temperature steam service 1300°F to 1450°F (704°C to 788°C) arc presented. Boiler water carryover conditions led to steam-side salt deposits containing sodium, chlorine, and sulfur species. The unique conditions of extremely high temperatures and localized accumulation of aggressive salt species resulted in component failures that involved a molten salt attack mechanism not typically observed in steam-side environments. Keywords: Alloy 800H, UNS No. NO8810, UNS No. N08811, Incoloy 800H, HP-40, HP-40Nb, niobium modified HP-40, molten salt attack, mixed molten salt attack, steam-side failures, iron-nickel-chromium alloys.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for Hot Corrosion of Nickel-Chromium Alloys in a Molten Eutectic Salt Environment
Available for download

51316-7824-Hot Corrosion of Nickel-Chromium Alloys in a Molten Eutectic Salt Environment

Product Number: 51316-7824-SG
ISBN: 7824 2016 CP
Author: Vilupanur Ravi
Publication Date: 2016
$20.00
Picture for Suitability of High Alloyed Materials in Molten Salts at 600 °C
Available for download

51316-7363-Suitability of High Alloyed Materials in Molten Salts at 600 °C

Product Number: 51316-7363-SG
ISBN: 7363 2016 CP
Author: Ralph Baessler
Publication Date: 2016
$20.00

Due to the composition of heat transmission media and temperatures, service conditions in solar facilities are, in many cases, extreme in terms of corrosion. By electrochemical measurements and exposure tests, the suitability of two alloys - X8NiCrSi38-18() and NiCr25FeAlYB - in molten nitrate salt (60 % NaNO3/40 % KNO3) was characterized at 600 °C.
Picture for Effect of Chloride Content on The Corrosion Behavior of Ferritic and Austenitic Steels in Molten Sol
Available for download

51316-7494-Effect of Chloride Content on The Corrosion Behavior of Ferritic and Austenitic Steels in Molten Solar Salts

Product Number: 51316-7494-SG
ISBN: 7494 2016 CP
Author: Ali Soleimani Dorcheh
Publication Date: 2016
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support