96442 CHLORIDATION-OXIDATION OF Fe-Cr AND Ni-Cr ALLOYS AT 800°C

Picture for 96442 CHLORIDATION-OXIDATION OF Fe-Cr AND Ni-Cr
Available for download
Product Number: 51300-96442-SG
ISBN: 96442 1996 CP
Author: Xuejin Zheng, Robert A. Rapp
$0.00
$20.00
$20.00
The chlorination-oxidation behavior of Fe-Cr (0-25 wt%Cr) and Ni-Cr (0-20wt%Cr) alloys was studied at 800°C in three different H2-HCl-H2O(V) environments. In a low HCl and low H2O(v) environment, where Cr2O3 is thermodynamically stable, the corrosion resistance of the Fe-Cr alloys increased with increasing Cr content in the alloys. In a high HCI and high H2O(v) environment, where FeCr2O4 is stable and CrCl2 is metastable, the corrcsion resistance of the Fe-Cr alloys depended similarly on the Cr content. Low-Cr Fe-Cr alloys exhibited large weight losses, while Fe-Cr alloys with higher than 19wt%Cr showed good corrosion resistance. In an environment of high HCI in the absence of H2O(v), the evaporative corrosion rate was fast and limited by gas phase diffusion, and independent of the Cr content in the Fe-Cr alloys. Ni and Ni-Cr alloys generally showed good corrosion resistance in the environments of high H2O(v) because of the low NiCl2 vapor pressure and formation of a protective Cr2O3 scale. However, in the environment of high HCl in the absence of H2O(v), selective evaporation of CrCl 2 occurs, which results in Cr depletion and even networks of voids for a high-Cr Ni-Cr alloy. Keywords: chlorination, oxidation, HCI, Fe-Cr alloys, Ni-Cr alloys, high temperature corrosion
The chlorination-oxidation behavior of Fe-Cr (0-25 wt%Cr) and Ni-Cr (0-20wt%Cr) alloys was studied at 800°C in three different H2-HCl-H2O(V) environments. In a low HCl and low H2O(v) environment, where Cr2O3 is thermodynamically stable, the corrosion resistance of the Fe-Cr alloys increased with increasing Cr content in the alloys. In a high HCI and high H2O(v) environment, where FeCr2O4 is stable and CrCl2 is metastable, the corrcsion resistance of the Fe-Cr alloys depended similarly on the Cr content. Low-Cr Fe-Cr alloys exhibited large weight losses, while Fe-Cr alloys with higher than 19wt%Cr showed good corrosion resistance. In an environment of high HCI in the absence of H2O(v), the evaporative corrosion rate was fast and limited by gas phase diffusion, and independent of the Cr content in the Fe-Cr alloys. Ni and Ni-Cr alloys generally showed good corrosion resistance in the environments of high H2O(v) because of the low NiCl2 vapor pressure and formation of a protective Cr2O3 scale. However, in the environment of high HCl in the absence of H2O(v), selective evaporation of CrCl 2 occurs, which results in Cr depletion and even networks of voids for a high-Cr Ni-Cr alloy. Keywords: chlorination, oxidation, HCI, Fe-Cr alloys, Ni-Cr alloys, high temperature corrosion
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 96443 CHLORINATION-OXIDATION OF COMMERCIAL
Available for download

96443 CHLORINATION-OXIDATION OF COMMERCIAL AUSTENITIC ALLOYS AT 800°C

Product Number: 51300-96443-SG
ISBN: 96443 1996 CP
Author: Xuejin Zheng, Robert A. Rapp
$20.00
Picture for 96439 Influence of Alloying Elements on
Available for download

96439 Influence of Alloying Elements on the Chlorination Behaviour of Nickel- and Iron-Based , Alloys

Product Number: 51300-96439-SG
ISBN: 96439 1996 CP
Author: D. C. Agarwal, U. Brill, J. Klower
$20.00
Picture for 96446 MATERIALS LIMITATIONS IN HIGH TEMPERATURE
Available for download

96446 MATERIALS LIMITATIONS IN HIGH TEMPERATURE CHLORINATING ENVIRONMENTS

Product Number: 51300-96446-SG
ISBN: 96446 1996 CP
Author: J.J. Barnes
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support