96329 EVALUATION OF SELECTED EPOXY-COATED REINFORCING STEELS

Picture for 96329 EVALUATION OF SELECTED EPOXY-COATED
Available for download
Product Number: 51300-96329-SG
ISBN: 96329 1996 CP
Author: H. Chen, H.G. Wheat
Industry: Highways & Bridges
$0.00
$20.00
$20.00
Epoxy-coated reinforcing steel (ECR) with nine kinds of coater/powder/steel/size combinations were evaluated based on their performance in resisting corrosion. Specimens prepared from these bars were characterized with regard to their coating thicknesses and surface conditions before being immersed in sodium chloride solution. Subsequently, electrochemical impedance spectroscopy (EIS) scans and polarization resistance measurements were performed periodically during approximately 200 days of exposure. In the case of EIS, coating degradation could be detected at a very early stage; and a great variation in the performance between ECR of different coater/powder/steel/size combinations was observed. The specimens were ranked based on their impedance responses and an attempt was made to correlate the ECR’S performance with their coating characteristics. Key Words: corrosion, reinforcing steel, epoxy, coating, electrochemical impedance spectroscopy, and polarization resistance
Epoxy-coated reinforcing steel (ECR) with nine kinds of coater/powder/steel/size combinations were evaluated based on their performance in resisting corrosion. Specimens prepared from these bars were characterized with regard to their coating thicknesses and surface conditions before being immersed in sodium chloride solution. Subsequently, electrochemical impedance spectroscopy (EIS) scans and polarization resistance measurements were performed periodically during approximately 200 days of exposure. In the case of EIS, coating degradation could be detected at a very early stage; and a great variation in the performance between ECR of different coater/powder/steel/size combinations was observed. The specimens were ranked based on their impedance responses and an attempt was made to correlate the ECR’S performance with their coating characteristics. Key Words: corrosion, reinforcing steel, epoxy, coating, electrochemical impedance spectroscopy, and polarization resistance
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 96325 COATING DISBANDMENT IN EPOXY-COATED
Available for download

96325 COATING DISBANDMENT IN EPOXY-COATED REINFORCING STEEL IN CONCRETE – FIELD OBSERVATIONS

Product Number: 51300-96325-SG
ISBN: 96325 1996 CP
Author: Alberto A. Sagues, Rodney G. Powers
$20.00
Picture for 96331 ANALYSIS OF POLARIZATION DECAY OF
Available for download

96331 ANALYSIS OF POLARIZATION DECAY OF REINFORCED CONCRETE IN SALTWATER

Product Number: 51300-96331-SG
ISBN: 96331 1996 CP
Author: Ashok Kumar, Jeffrey H. Boy
$20.00
Picture for 01642 CORROSION PERFORMANCE OF EPOXY-COATED
Available for download

01642 CORROSION PERFORMANCE OF EPOXY-COATED

Product Number: 51300-01642-SG
ISBN: 01642 2001 CP
Author: Alberto A. Sagues, Rodney G. Powers and Richard Kessler
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support