96248 Hydrogen Trapping Sites in High-strength Steels at Delayed Fracture

Picture for 96248 Hydrogen Trapping Sites in High-strength
Available for download
Product Number: 51300-96248-SG
ISBN: 96248 1996 CP
Author: Kenichi Takai, Jun’ichi Seki and Yoshikazu Homma
$0.00
$20.00
$20.00
Hydrogen trapping sites in high-strength steels hardened by cold drawing (PC Wire) and heat treatment (PC Bar) were investigated using thermal resorption spectroscopey (TDS ) and secondary ion mass spectrometry (SIMS). Both steels were stressed and dipped in 2090 NH4SCN solution at 323K to occlude hydrogen for TDS analysis, whereas they were stressed and dipped in D2O and 20% NH4SCN solution at 323K to occlude deuterium for SIMS analysis. TDS analysis shows that PC Wire occludes hydrogen fit the peaks of 470 K and 630 K, whereas PC Bar mainly occludes hydrogen at 470 K and slightly at 630 K. SIMS analysis makes it possible to observe the trapping sites of deuterium instead of hydrogen in high-strength steels. PC Wire traps deuteriurn along the drawing direction. PC Bar traps deuterium at the grain boundaries and on the inclusions. The correspondence between TDS and SIMS shows that hydrogen at 470 K is evolved from the matrix that includes dislocations and grain boundaries. In contrast, hydrogen at 630 K is evolved from inclusions and segregation of P. Keywords: delayed fracture, hydrogen, deuterium, high-strength, TDS. SIMS
Hydrogen trapping sites in high-strength steels hardened by cold drawing (PC Wire) and heat treatment (PC Bar) were investigated using thermal resorption spectroscopey (TDS ) and secondary ion mass spectrometry (SIMS). Both steels were stressed and dipped in 2090 NH4SCN solution at 323K to occlude hydrogen for TDS analysis, whereas they were stressed and dipped in D2O and 20% NH4SCN solution at 323K to occlude deuterium for SIMS analysis. TDS analysis shows that PC Wire occludes hydrogen fit the peaks of 470 K and 630 K, whereas PC Bar mainly occludes hydrogen at 470 K and slightly at 630 K. SIMS analysis makes it possible to observe the trapping sites of deuterium instead of hydrogen in high-strength steels. PC Wire traps deuteriurn along the drawing direction. PC Bar traps deuterium at the grain boundaries and on the inclusions. The correspondence between TDS and SIMS shows that hydrogen at 470 K is evolved from the matrix that includes dislocations and grain boundaries. In contrast, hydrogen at 630 K is evolved from inclusions and segregation of P. Keywords: delayed fracture, hydrogen, deuterium, high-strength, TDS. SIMS
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 96247 A NEW METHOD FOR IDENTIFICATION OF THE
Available for download

96247 A NEW METHOD FOR IDENTIFICATION OF THE MECHANISM OF CORROSION FATIGUE CRACK GROWTH

Product Number: 51300-96247-SG
ISBN: 96247 1996 CP
Author: S. A. Shipilov
$20.00
Picture for 96251 SIMULATION OF CHANGES IN STRESS
Available for download

96251 SIMULATION OF CHANGES IN STRESS CORROSION CRACKING ENVIRONMENTS IN ANAEROBIC CO2 RICH NEAR-NEUTRAL BULK SOLUTIONS

Product Number: 51300-96251-SG
ISBN: 96251 1996 CP
Author: M.J. Wilmott, M.K.Watson, R.W. Evitts
$20.00
Picture for 96262 IMPACT OF LONG TERM EXPOSURE ON
Available for download

96262 IMPACT OF LONG TERM EXPOSURE ON CORROSION FATIGUE CRACK GROWTH OF LOW ALLOY STEELS

Product Number: 51300-96262-SG
ISBN: 96262 1996 CP
Author: A. J. Griffiths, A. Tumbull
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support