96093 CHARACTERISTICS OF LEAD INDUCED STRESS CORROSION CRACKING OF ALLOY 690 IN HIGH TEMPERATURE

Picture for 96093 CHARACTERISTICS OF LEAD INDUCED STRESS
Available for download
Product Number: 51300-96093-SG
ISBN: 96093 1996 CP
Author: Koo-Kab Chung, Jae-Kyoo Lim, Yutaka Watanabe, Tetsuo Shoji
$0.00
$20.00
$20.00
Slow strain rate tests (SSRT) were conducted on alloy 690 in various lead chloride solutions and metal lead added to 100ppm chloride solution at 288°C. The corrosion potential(rest potential) for the alloy was measured with SSRT tests. The cracking was observed by metallographlc examination and electron probe micro analyser. Also, the corrosion behavior of the alloy was evaluated by anodic Dokirized measurement at 30°C. Resulting from the tests, cracking was characterized by cracking behavior, crack length and crack growth rate, and lead effects on cracking, The cracking was mainly intergranular in mode, approximately from 60 urn to 450 urn in crack length, and approximately ...
Slow strain rate tests (SSRT) were conducted on alloy 690 in various lead chloride solutions and metal lead added to 100ppm chloride solution at 288°C. The corrosion potential(rest potential) for the alloy was measured with SSRT tests. The cracking was observed by metallographlc examination and electron probe micro analyser. Also, the corrosion behavior of the alloy was evaluated by anodic Dokirized measurement at 30°C. Resulting from the tests, cracking was characterized by cracking behavior, crack length and crack growth rate, and lead effects on cracking, The cracking was mainly intergranular in mode, approximately from 60 urn to 450 urn in crack length, and approximately ...
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 96094 Detection of Localized and General Corrosion
Available for download

96094 Detection of Localized and General Corrosion of Mild Steel in Simulated Defense Nuclear Waste Solutions Using Electrochemical Noise Analysis

Product Number: 51300-96094-SG
ISBN: 96094 1996 CP
Author: D. F. Wilson, G. E. C. Bell, G. L. Edgemon, S.J. Pawel
$20.00
Picture for 96088 ASPECTS AND MECHANISMS OF AUSTENITIC
Available for download

96088 ASPECTS AND MECHANISMS OF AUSTENITIC STAINLESS STEEL CORROS1ON IN CASE OF SODIUM LEAKS UNDER MINERAL WOOL INSULATION

Product Number: 51300-96088-SG
ISBN: 96088 1996 CP
Author: C. Bertrand, A. Ardellier
$20.00
Picture for 96087 THE STABILITY OF NITRATE IN HIGH
Available for download

96087 THE STABILITY OF NITRATE IN HIGH TEMPERATURE WATER

Product Number: 51300-96087-SG
ISBN: 96087 1996 CP
Author: Thomas M. Angeliu, Young J. Kim, Peter L. Andresen, Dale F. Taylor
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support