96069 PROTOTYPE SULFIDE STRESS CRACKING TESTING OF HIGH STRENGTH OIL COUNTRY TUBULAR GOODS

Picture for 96069 PROTOTYPE SULFIDE STRESS CRACKING
Available for download
Product Number: 51300-96069-SG
ISBN: 96069 1996 CP
Author: J.P. FRICK, GRAHAM ELLIOT, ROBERT M. SHIVERS
$0.00
$20.00
$20.00
High pressure full size prototype sulfide stress cracking (SSC) tests of C90, C100, and C110 casing were conducted in NACE TM0177 Method A SCC test enviornment followed by failure analysis. The NACE TM0177 Method A SCC test environment was also used to determine smooth tensile sample SSC threshold data for the materials. An alternate environment consisting of 10% H2S and 90% N2 was also used to conduct prototype tests. The Von Mises threshold stress determined from the prototype samples was consistently less than the threshold stress determined by using NACE TM0177 Method A. It is concluded that the NACE Method A test does not provide the lower bound of the threshold stress compared to prototype test samples. Keywords: Hydrogen sulfide, casing, sour gas, corrosive, cracking, oil wells, gas wells
High pressure full size prototype sulfide stress cracking (SSC) tests of C90, C100, and C110 casing were conducted in NACE TM0177 Method A SCC test enviornment followed by failure analysis. The NACE TM0177 Method A SCC test environment was also used to determine smooth tensile sample SSC threshold data for the materials. An alternate environment consisting of 10% H2S and 90% N2 was also used to conduct prototype tests. The Von Mises threshold stress determined from the prototype samples was consistently less than the threshold stress determined by using NACE TM0177 Method A. It is concluded that the NACE Method A test does not provide the lower bound of the threshold stress compared to prototype test samples. Keywords: Hydrogen sulfide, casing, sour gas, corrosive, cracking, oil wells, gas wells
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 96072 PRELIMINARY INVESTIGATION OF HYDROGEN
Available for download

96072 PRELIMINARY INVESTIGATION OF HYDROGEN UPTAKE AND CRACKING IN 22 Cr DUPLEX STAINLESS STEEL UNDER GALVANIC COUPLING CONDITIONS

Product Number: 51300-96072-SG
ISBN: 96072 1996 CP
Author: A. J. Griffiths, A. Tumbull
$20.00
Picture for 96077 CORROSION PROPERTY OF API AND MODIFIED
Available for download

96077 CORROSION PROPERTY OF API AND MODIFIED 13CR STEELS IN OIL AND GAS ENVIRONMENT

Product Number: 51300-96077-SG
ISBN: 96077 1996 CP
Author: H.Kaneta, S.Sakamoto, K.Maruyama
$20.00
Picture for 96076 EFFECT OF ENVIRONMENTAL FACTORS ON
Available for download

96076 EFFECT OF ENVIRONMENTAL FACTORS ON DOWNHOLE SOUR GAS CORROSION

Product Number: 51300-96076-SG
ISBN: 96076 1996 CP
Author: Gerdt Wilken
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support