11095 Effect of Titanium Content on Hydrogen Induced Cracking of High Strength Low Alloy Welds in the H2S Containing Environment

Picture for 11095 Effect of Titanium Content on Hydrogen Induced Cracking of High Strength Low Alloy Welds
Available for download
Product Number: 51300-11095-SG
ISBN: 11095 2011 CP
Author: Afshin Zandipour, Alireza Khoshakhlagh, and Afshin Erfanfar
Publication Date: 2011
$0.00
$20.00
$20.00
The microstructure and hydrogen induced cracking of SAW welds in API 5L X70 grades with different amount of titanium were studied. The investigation was carried out on the base metal, heat affected zone and weld metal with three different titanium amounts in weld metal containing 1.4%Mn and 1.9%Mn respectively. The results showed that the centerline segregation region of the base metal was sensitive to hydrogen induced cracking while the heat affected zone did not show any failure. Furthermore, were observed that with addition of titanium, the formation of acicular ferrite in the microstructure and hardness values were increased and stress oriented hydrogen induced cracks appeared in the weld metal. The optimum combination of the microstructure and hydrogen induced cracking resistance was observed in 1.4%Mn-0.11%Ti and 1.9%Mn-0.05 Ti% respectively.

Keywords: Microstructure, Hydrogen Induced Cracking, Titanium, Acicular ferrite
The microstructure and hydrogen induced cracking of SAW welds in API 5L X70 grades with different amount of titanium were studied. The investigation was carried out on the base metal, heat affected zone and weld metal with three different titanium amounts in weld metal containing 1.4%Mn and 1.9%Mn respectively. The results showed that the centerline segregation region of the base metal was sensitive to hydrogen induced cracking while the heat affected zone did not show any failure. Furthermore, were observed that with addition of titanium, the formation of acicular ferrite in the microstructure and hardness values were increased and stress oriented hydrogen induced cracks appeared in the weld metal. The optimum combination of the microstructure and hydrogen induced cracking resistance was observed in 1.4%Mn-0.11%Ti and 1.9%Mn-0.05 Ti% respectively.

Keywords: Microstructure, Hydrogen Induced Cracking, Titanium, Acicular ferrite
Product tags
Also Purchased
Picture for Effect of Microstructure on Hydrogen Induced Cracking and Sulfide Stress Cracking Property of Pressu
Available for download

51312-01204-Effect of Microstructure on Hydrogen Induced Cracking and Sulfide Stress Cracking Property of Pressu

Product Number: 51312-01204-SG
ISBN: 01204 2012 CP
Author: Sung Jin Kim
Publication Date: 2012
$20.00
Picture for 11093 Development of New Corrosion Inhibitor to Prevent Black Powder Formation Using Quartz Crystal
Available for download

11093 Development of New Corrosion Inhibitor to Prevent Black Powder Formation Using Quartz Crystal Microbalance Technique

Product Number: 51300-11093-SG
ISBN: 11093 2011 CP
Author: Kyle Cattanach, Vladimir Jovancicevic, Sunder Ramachandran and Abdelmounam M. Sherik
Publication Date: 2011
$20.00
Picture for 11091 Affect of Black Powder on Inline Inspection Accuracy
Available for download

11091 Affect of Black Powder on Inline Inspection Accuracy

Product Number: 51300-11091-SG
ISBN: 11091 2011 CP
Author: Jaime P. Perez
Publication Date: 2011
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support