10300 Effect of CO2 on Near-Neutral Ph Stress Corrosion Cracking Initiation of Pipeline Steel

Picture for 10300 Effect of CO2 on Near-Neutral Ph Stress Corrosion Cracking Initiation of Pipeline Steel
Available for download
Product Number: 51300-10300-SG
ISBN: 10300 2010 CP
Author: Abdoulmajid Eslami, Weixing Chen, Robert Grant Worthingham, Richard Kania and Jenny Been
Publication Date: 2010
$0.00
$20.00
$20.00
Near-neutral-pH SCC has been one of the major remaining concerns to pipeline safe operation. In order to improve our understanding of its initiation mechanism a comprehensive testing setup was used in this study. It was found that the initial near-neutral-pH environment under the disbonded coating of pipeline steel can vary significantly from near-neutral to high pH values. The pH value was strongly affected by CO2 availability and the level of cathodic protection. When cyclic loading was applied in the stress corrosion cracking initiation tests, based on the local environment under the disbonded coating, different products from corrosion pits to surface micro-cracks were initiated on pipe surface up the gradient of cathodic protection.

Key Words: Cathodic Protection, Crack Initiation, Cyclic Loading, Near-Neutral pH, Pipeline Steel, SCC Initiation.
Near-neutral-pH SCC has been one of the major remaining concerns to pipeline safe operation. In order to improve our understanding of its initiation mechanism a comprehensive testing setup was used in this study. It was found that the initial near-neutral-pH environment under the disbonded coating of pipeline steel can vary significantly from near-neutral to high pH values. The pH value was strongly affected by CO2 availability and the level of cathodic protection. When cyclic loading was applied in the stress corrosion cracking initiation tests, based on the local environment under the disbonded coating, different products from corrosion pits to surface micro-cracks were initiated on pipe surface up the gradient of cathodic protection.

Key Words: Cathodic Protection, Crack Initiation, Cyclic Loading, Near-Neutral pH, Pipeline Steel, SCC Initiation.
Product tags
Also Purchased
Picture for 08265 Modeling of Carbonate-Bicarbonate Stress Corrosion Cracking of Pipeline Steels
Available for download

08265 Modeling of Carbonate-Bicarbonate Stress Corrosion Cracking of Pipeline Steels

Product Number: 51300-08265-SG
ISBN: 08265 2008 CP
Author: Robert A. Cottis and Maftah H. Alkathafi
Publication Date: 2008
$20.00

This project has been concerned with the physical and numerical modeling of the conditions developed under disbonded coatings on steel, with a view to understanding the processes responsible for the conditions that lead to stress corrosion cracking.
Picture for 10297 Environmental Effects on the Susceptibility & Crack Growth of Near Neutral Ph Stress Corrosion
Available for download

10297 Environmental Effects on the Susceptibility and Crack Growth of Near Neutral Ph Stress Corrosion Cracking

Product Number: 51300-10297-SG
ISBN: 10297 2010 CP
Author: Jeffrey Xie, Chris Foy, Bob Worthingham and Mark Piazza
Publication Date: 2010
$20.00
Picture for 06175 Stress Corrosion Cracking of Pipeline Steel
Available for download

06175 Stress Corrosion Cracking of Pipeline Steel in Near-Neutral pH Environments

Product Number: 51300-06175-SG
ISBN: 06175 2006 CP
Author: Stefanie L. Asher, Jeffery A. Colwell, Preet M. Singh, Brian N. Leis
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support