10001 Studies on the Bond Durability Between the Steel and 3 Layers PE/PP Coatings in Hot/Wet Environment

Picture for 10001 Studies on the Bond Durability Between the Steel and 3 Layers PE/PP Coatings in Hot/Wet
Available for download
Product Number: 51300-10001-SG
ISBN: 10001 2010 CP
Author: Denis Melot
Publication Date: 2010
$0.00
$20.00
$20.00
For the last few years, an oil company has carried out laboratory testing of tri-layers PE and PP pipe coatings in hot wet environment.

The objective was to simulate the disbondment from the steel substrate noted in some cases in the field (with no corrosion associated), and understand the physico-chemical mechanism at the origin of the loss of adhesion experienced.

This paper will sum up the results obtained so far from this RD effort, with a special highlight on the following points :

?? Durability of the bond between the steel and the FBE primer/Influence of water diffusion ?? Influence of the FBE type and ageing temperature on the disbondment ?? Influence of internal stresses on the disbondment of three layers coatings.

Keywords : pipeline coating-hot water-ageing-durability
For the last few years, an oil company has carried out laboratory testing of tri-layers PE and PP pipe coatings in hot wet environment.

The objective was to simulate the disbondment from the steel substrate noted in some cases in the field (with no corrosion associated), and understand the physico-chemical mechanism at the origin of the loss of adhesion experienced.

This paper will sum up the results obtained so far from this RD effort, with a special highlight on the following points :

?? Durability of the bond between the steel and the FBE primer/Influence of water diffusion ?? Influence of the FBE type and ageing temperature on the disbondment ?? Influence of internal stresses on the disbondment of three layers coatings.

Keywords : pipeline coating-hot water-ageing-durability
Product tags
Also Purchased
Picture for 10002 Failure Analysis of Three Layer Polypropylene Pipeline Coatings
Available for download

10002 Failure Analysis of Three Layer Polypropylene Pipeline Coatings

Product Number: 51300-10002-SG
ISBN: 10002 2010 CP
Author: Ali Noor Moosavi, Benjamin T. A. Chang and Kamal Mohamed Morsi
Publication Date: 2010
$20.00

Three layer polypropylene (3LPP) pipeline coatings failed prematurely in the oilfields of Abu Dhabi in the United Arab Emirates (UAE). A failure investigation and analysis into this phenomenon was instigated. The coating disbondment has been found to be due to high residual stress concentration and adhesion loss.
Picture for Fusion Bonded Epoxy Coatings (FBE) and Disbondment
Available for download

Fusion Bonded Epoxy Coatings (FBE) and Disbondment

Product Number: 51316-7246-SG
ISBN: 7246 2016 CP
Author: Mehrooz Zamanzadeh
Publication Date: 2016
$20.00

In this paper, failure analysis methodology will be applied to the principal mechanisms by which FBE coatings fail during long term service; with specific application to case studies involving blistering. The case studies apply standard failure analysis techniques to determine the primary causes and modes of failures.
Picture for 06053 MULTI-LAYER PIPELINE COATING SYSTEMS
Available for download

06053 MULTI-LAYER PIPELINE COATING SYSTEMS: A NEW LOOK AT THE EVALUATION OF CERTAIN QC TESTS AND CRITICAL APPLICATION PARAMETERS FOR FBE PRIMERS

Product Number: 51300-06053-SG
ISBN: 06053 2006 CP
Author: Paul Partridge
Publication Date: 2006
$20.00

 This paper begins with a brief discussion of essential properties of all pipeline coatings, and a listing of multi-layer systems designed to meet specific needs. It then focuses on special considerations regarding application parameters for multi-layer systems that use fusionbonded epoxy as the primer.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support