09259 Deposit-Assisted Corrosion of Heat-Resistant Alloys

Picture for 09259 Deposit-Assisted Corrosion of Heat-Resistant Alloys
Available for download
Product Number: 51300-09259-SG
ISBN: 09259 2009 CP
Author: James Rakowski and David S. Bergstrom
Publication Date: 2009
$0.00
$20.00
$20.00
Chloride-based deposits can significantly accelerate the progress of elevated temperature degradation of stainless steels and nickel-base alloys. Such deposits are present in the byproducts of combustion of alternative fuels and are common in the environment experienced by hot automotive exhaust components. A test was developed to investigate the susceptibility of materials to attack under chloride salt deposits at elevated temperatures, using a sample incorporating stressed, unstressed, and welded segments. Both gravimetric and metal recession measurements were used to determine the progression of corrosion. Nickel-base alloys were found to be resistant to deposit-assisted attack, while common stainless steels were prone to scaling and exfoliation. Results will also be presented on recently developed higher-alloy content stainless steels which exhibit corrosion resistance similar to that of the nickel-base superalloys, and on lean austenitic stainless alloys intended as replacements for traditional austenitic stainless steels.

Keywords: high temperature oxidation, corrosion, chloride salts
Chloride-based deposits can significantly accelerate the progress of elevated temperature degradation of stainless steels and nickel-base alloys. Such deposits are present in the byproducts of combustion of alternative fuels and are common in the environment experienced by hot automotive exhaust components. A test was developed to investigate the susceptibility of materials to attack under chloride salt deposits at elevated temperatures, using a sample incorporating stressed, unstressed, and welded segments. Both gravimetric and metal recession measurements were used to determine the progression of corrosion. Nickel-base alloys were found to be resistant to deposit-assisted attack, while common stainless steels were prone to scaling and exfoliation. Results will also be presented on recently developed higher-alloy content stainless steels which exhibit corrosion resistance similar to that of the nickel-base superalloys, and on lean austenitic stainless alloys intended as replacements for traditional austenitic stainless steels.

Keywords: high temperature oxidation, corrosion, chloride salts
Product tags
Also Purchased
Picture for 05288 Test Methodologies and Field Verification of
Available for download

05288 Test Methodologies and Field Verification of Corrosion Inhibitors to Address under Deposit Corrosion in Oil and Gas Production Systems

Product Number: 51300-05288-SG
ISBN: 05288 2005 CP
Author: Han De Reus, Edwin L.J.A. Hendriksen, and Marc Wilms, Shell Global Solutions International; Yahya N.
$20.00
Picture for 09338 Heat Treatment Issues on Stainless Steel Heat Exchanger Tubes
Available for download

09338 Heat Treatment Issues on Stainless Steel Heat Exchanger Tubes

Product Number: 51300-09338-SG
ISBN: 09338 2009 CP
Author: Cathleen A. Shargay, Karly Moore and John J. Wodarcyk
Publication Date: 2009
$20.00

Proper heat treatment on stainless steel (SS) heat exchanger tubes is very important to obtain the expected stress corrosion cracking (SCC) and corrosion resistance of the material. This paper will discuss three recent issues that have arisen on this topic.
Picture for 11262 Under-Deposit Corrosion Failure of a Compressor
Available for download

11262 Under-deposit Corrosion Failure of a Compressor after Stage Cooler at an NGL Plant- A Case Study

Product Number: 51300-11262-SG
ISBN: 2011 11262 CP
Author: S. A. Al-Dossary, A. K. Debbert and M. A. Al- Mubayidh
Publication Date: 2011
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support