08668 Effects of Slurry pH on the Surface Mechanical Properties and Erosion Corrosion Resistance

Picture for 08668 Effects of Slurry pH on the Surface Mechanical Properties and Erosion Corrosion Resistance
Available for download
Product Number: 51300-08668-SG
ISBN: 08668 2008 CP
Author: Baotong Lu, Ke Wang, Xuemei Wan, and Jingli Luo
Publication Date: 2008
$0.00
$20.00
$20.00
Effects of anodic dissolution in corrosive slurries with different chemical compositions and pHs on the in-situ surface mechanical properties and slurry erosion-corrosion resistance of carbon steel were investigated. The experimental measurements indicate the existence of corrosion-enhanced erosion because the erosion is accelerated by the anodic current and it depends heavily on the slurry pH and chemistry. The in-situ nanoindentation shows that the presence of anodic current on the surface reduces the surface hardness. When the anodic current density was held unchanged, both the corrosion-enhanced erosion in acidic slurries and the corrosion-induced surface hardness degradation in the acidic solutions were much more pronounced than those in neutral and alkaline slurries/solutions. In the neutral and alkaline media, the corrosion-enhanced erosion and the in-situ surface hardness degradation were hardly affected by the chemical composition of aqueous media but a remarkable impact of chemical composition was observed when corrosive media are acidic.
Effects of anodic dissolution in corrosive slurries with different chemical compositions and pHs on the in-situ surface mechanical properties and slurry erosion-corrosion resistance of carbon steel were investigated. The experimental measurements indicate the existence of corrosion-enhanced erosion because the erosion is accelerated by the anodic current and it depends heavily on the slurry pH and chemistry. The in-situ nanoindentation shows that the presence of anodic current on the surface reduces the surface hardness. When the anodic current density was held unchanged, both the corrosion-enhanced erosion in acidic slurries and the corrosion-induced surface hardness degradation in the acidic solutions were much more pronounced than those in neutral and alkaline slurries/solutions. In the neutral and alkaline media, the corrosion-enhanced erosion and the in-situ surface hardness degradation were hardly affected by the chemical composition of aqueous media but a remarkable impact of chemical composition was observed when corrosive media are acidic.
Product tags
Also Purchased
Picture for 08572 Erosion-Corrosion in Disturbed Liquid/Particle Flow
Available for download

08572 Erosion-Corrosion in Disturbed Liquid/Particle Flow

Product Number: 51300-08572-SG
ISBN: 08572 2008 CP
Author: Joshua Addis, Srdjan Nesic, and Bruce Brown
Publication Date: 2008
$20.00
Picture for 07685 Assessing the Erosion Corrosion Properties of Materials for Slurry Transportation and Processi
Available for download

07685 Assessing the Erosion Corrosion Properties of Materials for Slurry Transportation and Processing in the Oil Sands Industry

Product Number: 51300-07685-SG
ISBN: 07685 2007 CP
Author: Mark Jones and Rees Llewellyn
Publication Date: 2007
$20.00
Picture for Erosion-Corrosion Study of Oilfield Materials Due to Liquid Impact
Available for download

Erosion-Corrosion Study of Oilfield Materials Due to Liquid Impact

Product Number: 51315-6136-SG
ISBN: 6136 2015 CP
Author: Hadi Arabnejad Khanouki
Publication Date: 2015
$20.00

The goal of this work is to determine erosion-corrosion damage caused by liquid impact in the oil and gas industry.

Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support